混凝土寿命预测模型的研究进展.pdfVIP

混凝土寿命预测模型研究进展 张文华 周 云 焦楚杰 （广州大学土木工程学院 广州 510006 ） 摘要：综观混凝土寿命预测模型的研究，从单因素、多因素耦合作用下混凝土预测模型二个方面介绍该领 域的国内外最新研究进展，分别从碳化模型、硫酸盐侵蚀模型及cl-侵蚀模型进行深入的阐述，分析了现有 混凝土寿命预测模型存在的局限，并指出了进一步研究中需要解决和关注的问题，为建立更准确的混凝土 寿命预测模型提供了参考意见。 关键词：寿命预测 耐久性 预测模型 进展 中图分类号：TU 528 Research Progress in Service-life Prediction Model for the Concrete ZHANG Wenhua ZHOU Yun JIAO Chujie ( School of Civil engineering, Guangzhou University, Guangzhou 510006) Abstract: An overview on the research of the life prediction of concrete, the latest development of the service life prediction of concrete under single factor and combined action of durability factors were presented, and the carbonation model、sulfate attack model and chloride ion penetration model were particular described. The shortage of the existing prediction model were analyzed. The problems in future research were brought forward for the building of the life precision prediction of concrete. Key words: service-life prediction ; durability; prediction model; development 0 前言 分发挥其功能、最大限度地利用资源，使建 吴中伟院士曾提出[1] ：经妥善设计和优 筑业管理、规划、设计与使用部门做到有的 质施工的HPC 结构的安全使用期应不低于 放矢，对混凝土进行寿命评估显得异常重 100 年，在正常环境中使用的结构的安全使 要。 用期应达 200 年，特殊重要工程在采取必要 混凝土的使用寿命受多种因素影响，其 [5] 措施后的安全使用期应达 300 年。然而，如 中包括力学因素、环境因素及材料因素等 ， 果对高性能混凝土寿命没有一个较为准确 其中环境因素里又分为二氧化碳、硫酸盐、 的估计，耐久性良好的高性有混凝土建筑过 cl − 、冻融循环等不同的侵蚀环境。对于混 早地拆除，势必造成大量资源的浪费，与“绿 色混凝土”这一称谓背道而驰。另一方面， 凝土寿命的评估主要从这些影响因素出发， 混凝土建筑超期服役会造成严重的安全隐 根据不同环境中相关的侵蚀机理建立对应 [2-4] 患 。 的数学模