（学士）学位论文 全水发泡在阻燃聚氨酯硬泡中的应用研究.docVIP

高分子材料与工程毕业论文 专业：高分子材料与工程　 题目：全水发泡在阻燃聚氨酯硬泡中的应用研究 摘要 采用多元醇、异氰酸酯、催化剂、发泡剂和阻燃剂等为原料制备了全水发泡阻燃聚氨酯硬质泡沫（PURF），讨论了聚醚多元醇种类、催化剂、发泡剂、异氰酸酯指数以及阻燃剂对聚氨酯硬质泡沫性能的影响。结果表明 ，聚酯多元醇能够改善泡孔结构 ，但降低压缩强度和尺寸稳定性；不同催化剂复配 ，可以控制发泡工艺;水发泡剂与泡沫的密度、泡孔结构、力学性能有关；异氰酸酯指数在1.1～1.2时 ，泡沫的压缩强度、尺寸稳定性等较好;三(2-氯异丙基) 磷酸酯(TCPP)可赋予聚氨酯硬质泡沫一定的阻燃性，但对泡体结构、压缩强度和尺寸稳定性有影响。 关键词 ABSTRACT The water-blown rigid polyurethane flame-retardant foam(PURF) was prepared by polyol, isocyanate , catalyst ,blowing agents and flame retardants as raw materials,in this pape. The types of polyrther polyols, catalysts, blowing agents,isocyanate index and fire retardant on the PURF performance were investgated. The results show that the polyester polyol can improve the cell structure, but reduce the compression strength and dimensional stability; different catalyst compound, can control the foaming process; water foaming agent and foam density, cell structure, the mechanical properties; isocyanate index of 1.1 to 1.2, the foam compression strength, good dimensional stability, etc.; Tris-(2-chloroisopropyl)phosphate phosphate (TCPP) flame retardant may be given to PURF certain, but on the bubble structure, compressive strength dimensional stability, and impact. Keywords：Rigid Polyurethane Foam,Water-blown, Flame retardant  目 录 摘要 I ABSTRACT II 第一章 前言 1 1.1 聚氨酯概况 1 1.1.1聚氨酯简介及其应用 1 1.2 聚氨酯的发展现状及趋势 2 1.3硬质聚氨酯泡沫塑料 3 1.3.1硬质聚氨酯泡沫塑料的性能特点 3 1.3.2聚氨酯泡沫塑料的制备 3 1.3.3聚氨酯硬泡的应用 4 1.4 硬泡全水发泡技术 4 1.5 全水发泡在阻燃聚氨酯硬泡的研究 5 第二章 实验部分 6 2.1 实验仪器及药品 6 2.2 基本化学反应及泡沫形成原理 7 2.3硬泡合成过程及样品的制备 7 2.4抗压强度 8 2.5表观密度（GB/T 6343-1995） 8 2.6吸水率的测定 9 第三章 结果与讨论 10 3.1 配方影响因素 10 3.1.1多元醇的选择及用量对泡沫性能的影响 10 3.1.2异氰酸酯指数的确定 12 3.1.3水的量对聚氨酯泡沫性能的影响 13 3.1.4聚氨酯硬泡的阻燃性能 15 结 论 16 参考文献 17 致谢 18  第一章 前言 1.1 聚氨酯概况 1.1.1聚氨酯简介及其应用 聚氨酯是聚氨基甲酸酯的简称。凡是在高分子主链上含有许多重复的(-NHCOO-)氨基甲酸酯基团的高分子化合物通称为聚氨酯。一般聚氨酯系由二元或多元有机异氰酸酯与多元醇化合物（聚醚多元醇或聚酯多元醇）相互作用而得。根据所用原料官能度数目的不同可以制成线形结构或体形结构的高分子聚合物。由于聚合物的结构不同，性能也不一样。利用这样的性质，聚氨酯类聚合物可以分别制成塑料、橡胶、纤维、涂料、胶粘剂等[1]。近二十年来，聚氨酯在这几个方面的应用都发展很快，特