Al3+对掺Er3+溶胶凝胶玻璃发光性质的影响 潘新华 毛艳丽﹡林丙臣 (河南大学光学与光电子技术研究所, 开封 475004) 摘 要 通过sol-gel(溶胶-凝胶)方法制备了掺Er3+ 和Al3+的硅基玻璃，并研究了Al3+对Er3+发光性能的影响，结果显示掺Al3+后不但使样品中Er3+离子的最大掺杂浓度提高一倍，而且样品中Er3+离子的发光强度明显增强，是不掺Al3+的Er-硅基玻璃中Er3+离子发光强度的20多倍， 通过分析我们推测Er3+和Al3+之间并不是简单的能量传递关系。同时发现，在980nm波长激发，Er3+离子只有654nm一个波长的上转换荧光。 关 键 词：Sol-Gel；Er-硅基玻璃；Al3+ ；光谱特性 中图分类号：O 433 ? 4 64 文献识别码： The influence of Al3+ on Er3+ doped sol－gel derived silica glass and studies on their optical properties PAN Xin-hua , MAO Yan-li , LIN Bing-chen (Institute of Optics and Photoelectronic Technology of Henan University, Kaifeng 475004,China) Abstract: The silica glasses doped with Er3+ and Al3+ iones were synthesized through Sol-Gel process in this paper. The effect of Al3+ on luminescence properties of Er3+ was studied. The results show that the concentration of Er3+ in co-doped silica glass can be improved one time than Er-doped glass，and the intensity is 20 times than that of Al non-doped glass. We concluded that the relation between Al3+ and Er3+ is just not energy transfer。And we find that Er3+ iones have only an up- conversion emission at 654nm using 980nm excitation. Key words: Sol-Gel; Er-silica glass; Al3+; spectral properties 0引言 在镧系金属离子中，Er3+是发光性能比较好的稀土离子，它所发射的红外荧光（1532nm）具有单色性好，量子效率高等优点，因此，被广泛应用于各种领域的发光材料中，Er3+的能级已被研究得十分充分，Er3+的基态是4Ij (j=9/2、11/2、13/2、15/2)[1]。将Er3+的掺杂到硅基玻璃，可以在硅基玻璃中形成独立的发光中心，产生许多优良的机械性能和光学性能。但如何将它们均匀的掺杂到硅基玻璃中，存在许多困难，如析晶现象，高温操作等，但是，随着溶胶－凝胶技术的出现，这一系列的问题也随之迎刃而解。相对于熔融法而言，溶胶－凝胶法有如下优点：⑴操作温度远低于传统硅基玻璃的熔融温度；⑵可提高掺杂浓度,准确控制掺杂量；⑶在室温下液态混合,可达到分子水平的高度均一,大大提高掺杂的均匀性；⑷制备的材料大部分透明性好[2].即便如此，当Er3+的掺杂浓度超过0.5％（摩尔百分比）时，荧光强度逐渐降低，发生荧光浓度猝灭，本文就针对这一问题，在纯硅基的基础上引入Al3+离子（前驱体为Al(NO3)3·9H2O） 基金项目：河南省高校骨干教师资助项目,河南大学自然科学基金重点项目（04ZDZR002)1 样品制备和测试 1.1样品的制备 先将正硅酸乙酯(AR)在三次去离子水、无水乙醇(AR) 、盐酸(AR)的混合溶液中水解一小时,再加入适量的Al(NO3)3·9H2O,引入Al3+离子.等完全水解后再注入一定量的Er(NO3)3溶液.在室温下磁力搅拌三个小时,生成溶胶,然后倒入培养皿中放置干燥,直至变成凝胶.最后放入马弗炉中热处理,温度升至1000℃,升温速率0.1℃/min.通过变化Er(NO3)3的加入量,依次制得不同浓度下的各个样品,比例为摩尔比，其中， a# 95Si