304L无填丝焊接换热管母材环向开裂原因探讨.pdfVIP

304L 无填丝焊接换热管母材环向开裂原因探讨 镇海石化建安工程安装公司（宁波315207 ） 林天委 赖德海 摘 要：对304L 无填丝焊接换热管母材环向开裂处进行金相、能谱及断口扫描电镜分析，另外对管子未 开裂处进行机械性能和工艺性能试验。分析结果表明焊接管未开裂处的化学成分、机械(工艺)性能均符 合标准要求。但裂纹处能谱分析显示C 元素等有明显偏析，尤其是Cu、Pt 等元素含量畸高，而其它处 无此现象；裂纹处金相组织基本正常，断口为沿晶脆性断裂。 关键词：焊接换热管；环向开裂；沿晶脆性断裂；网状脆性薄膜；应力集中 CAUSATION ANALYSIS OF 304L WELDING RECUPERATOR TUBE PARENT METAL TRANSVERSE FRACTURE LIN TianWei Lai dehai (Quality inspect department，ZhenHai Refining Chemical Maintenance and Installation Co. ， ning bo china 315207) Abstract: This paper mainly analyzes the crack and fracture of 304L welding recuperator tube parent metal, by the Microscope 、Scans the electron microscope and Material testing machine 。the composition, Machine function (craft function) of whole jointing duct accord with the standards; But the crack place power spectrum analysis demonstrated the C element and so on has the obvious segregation, element content and so on Cu, Pt are unbalanced in particular high, but other place does not have this phenomenon; Crack place microstructure basic normal, fracture for along crystal brittle fracture. Key word: Welding recuperator tube; Link to dehiscence; Along crystal brittle fracture; Netted brittle thin film; Stress concentration 1 引言 材质为304L 的1.5mm 和 1.2mm 厚的带料在卷 制成Φ18×1.5 和Φ15×1.2 的焊接管后中水压试 验时母材出现开裂现象，另外焊接成品管在绕制管 过程中也出现开裂现象。裂纹为环向裂纹，部分裂 纹穿透管壁，部分裂纹未穿透管壁，裂纹基本上都 是从管子外壁起裂；如图1 所示。在卷管过程即存 在轴向拉应力又存在横向卷制应力和焊接热应力。 2 理化检验 图1-Φ19×1.5 焊接管开裂处 2.1 化学成分分析 对管子开裂处和完好处用DV－4 光谱分析仪分别进行了成分分析，结果表明不同点成 ＃ 分存在差异，但不明显，如表 1 所示。1 样上不同处在试验过程中发现Cu 元素含量最高 ＃ 点与最低点相差0.2%左右。2 样完好段和裂纹旁C 元素含量有微量的差异，但都在合格标 准范围内。从表中可看出材料各主要元素含量在宏观上每个试样都符合标准要求。 1 表1-裂纹附近化学成分 元素