提高滑动水口自动开浇率的研究.docVIP

提高钢包水口自动开浇率的研究 （） 摘　要：对钢包水口自动开浇研究，改进了座砖上水口。钢包水口自动开浇率90%以上，解决钢包水口自动开浇率低影响连铸连浇。 关键词：钢包；水口；座砖；自动开浇 Research on Improving Automatic Pouring Rate of Ladle Slip Nozzle (China International Steel Products Co.Ltd., Mawei 350015, Fuzhou Fujian China) Abstract：In order to solve the problem of low automatic pouring rate of ladle slip nozzle and make numerous burning what affecting continuous casting of CCM, the diversion sand is studied in the steel-making plant of Zhonggang, and the pocket brick and up-nozzle are improved, and the fill method are changed . The test has proved that the automatic pouring rate of ladle slip nozzle is up to 90%, the up-nozzle life is increased to 12 heats. The improvement of automatic pouring rate of ladle nozzle establishes basement for realizing non oxygen pouring and developing clean steel, and reduced workers working intensity greatly at the same time. Keywords：ladle；slip nozzle；pocket brick；automatic pouring 1 前言 　，对钢包水口自动开浇率提出了更高的要求。同时也是连铸采用长水口，实现全保护浇注的重要前提条件。，钢炼钢厂钢包滑动水口自开率低，针对现有条件，借鉴其他钢厂的成熟经验，对钢包滑动水口自动开浇技术进行系统、全面的研究， 2 现状分析 钢炼钢厂现有座炉，台四流小方坯连铸机，年钢产量万t以上，主要冶炼钢种有普碳、(45)优钢以及少量HRB系列等。2～3mm海砂（河砂）与石墨混匀而成（wSiO2不小于70%）由于钢包用座砖，引流砂中SiO2与座砖反应，在内壁形成“结瘤”，同时引流砂中SiO2还会与炉渣中FeO、MnO等发生反应，生成低熔点化合物MnO.SiO2和FeO.SiO2，将座砖水口内的引流砂粘附在一起，使得“结壳”变厚，流动性。颗粒级配加入操作等环节3　主要措施 3.1　引流砂的研究n(Fe,Mg)R2O4+O2→(n-4)(Fe,Mg)R2O4 +2Fe2O3+4R2O3 (1) 2Fe2O3+C→4FeO+CO2 (2) 4FeO+4R2O3→4FeR2O4(二次尖晶石) (3） 式中：R表示三价阳离子，C表示还原剂，n=4。 （1）为脱溶反应，（2）为还原反应。 由于引流砂添加了助烧结剂等添加剂，高温下二次尖晶石作用更加明显，助烧结剂的熔点较低，其作用主要是与铬铁矿等原料反应，由于加入量少，并在高温下与铬铁矿等反应生成耐火度较高的脆性新相，在铬铁矿颗粒之间起到粘结作用，在打开滑板瞬间，由于润滑剂的存在，水口下部没有烧结的引流砂，靠自身重力作用迅速流出，使大量的冷空气进入，造成引流砂烧结层上下两侧产生很大的热应力，热应力引起脆性烧结层裂纹迅速扩展，在钢水的静压力作用下烧结层完全被破坏，因而达到自动导流的目的。 3.1.3材质选择 硅质引流砂价格低廉，但其物理液相的温度较低，在1300℃左右就开始出现液相且随温度的升高、时间的延长出现的液相量也随之增加，从而导致引流砂液—固相混合层增厚，粘度增大，并且在高温下其体积膨胀较大，膨胀的结果是使引流砂更趋于致密，使引流砂的流动性变差，且热抗震性较好，导致钢水静压力较难冲破液—固相混合层，而达不到自动开浇的效果。而铬质引流砂物理液相的温度较高，在1400℃左右才出现液相，相应地所出现的液—固相混合层也较薄；同时由于铬质引流砂中含有一定量的碳，进一步提高其熔点，又由于碳与钢水不浸润，可以阻止钢水的渗透，并烧结成为脆而多孔隔热性较好的烧结层，铬质引流砂