粉煤灰对垃圾锚固材料性能的影响.pdfVIP

· 552 · 材料导报 2009年 11月第23卷专辑 l4 InfluenceofFlyAshon PropertiesofRubbishAnchoringM aterial ZHANG M ing，XU Lingling，ZHANG Zhibin (CollegeofMaterialScienceandEngineering，NanjingUniversityofTechnology，Nanjing210009) Abstract Theinfluenceofdifferentamountofflyashonpropertiesoftherubbishanchoringmaterialisin— vestigated．Theexperimentalresultsindicatethatthepozzolanicreactionofflyashtakesplaceafteracertainamountis addedintotheanchoringmateria1．Astheageisprolonged，thepermeabilityandmechanicalpropertiesoftheanchoring materialareimproved．Similarly，themoreamountofflyashisincorporated，thebetterthepemr eabilityoftheanchoring materia1willhe．Whiletheflyashisamounted24 ，thefluidityoftherubbishanchoringmaterialisoptima1．Sothean— ehoringmaterialcanbeappliedeasilytothesurfaceoftherubbishpiles． Keywords flyash，fluidity，mechanicalproperties，pozzolanicreaction，impemr eability 粉煤灰对垃圾锚固材料性能的影响 章 明，徐玲玲，张志宾 (南京工业大学材料学院，南京 210009) 摘要 研究了不同掺量的粉煤灰对垃圾锚固材料性能的影响，结果表明，锚固材料 中掺入一定量的粉煤灰后， 由于粉煤灰的火山灰反应，随着龄期的延长，抗渗能力和材料力学性能都有所提高；并且随着粉煤灰掺量的增加，锚 固材料的抗渗能力也将提高。当粉煤灰掺量为24 时，所得的锚固材料的流动度最佳，因此可以容易地被喷射到垃 圾堆表面以固结垃圾 。 关键词 粉煤灰 流动度 力学性能 火山灰反应 抗渗性能 tiousanchoringmaterialismainlycomposedofadhesives，water 0 Introduction andfibers。andtheadhesiveswithitsmasscontentofapproxi— Flyashhaseverbeenamassindustria1waste．Recentlyit mate40％～7O％canbedividedintoinorganicandorganicadhe— hasaccumulatedoveronebilliontons．Inthepast，flyashnoton— sires．Thewatercontentis30 ～6O oftheamountoftheto— lyoccupied ,1．argeamountofarea