喷瓷管线接头焊后涂层与基体的界面研究Ⅱ.pdfVIP

材料工程990208 材料工程 JOURNAL OF MATERIALS ENGINEERING 1999年 第2期 No.2 1999 喷瓷管线接头焊后涂层与基体的界面研究(Ⅱ) 王维东　王勇　何艳玲　李红林 ［摘要］　对焊接前后的氮气保护喷瓷管线分别进行了TEM试验。结果表明，焊接前 涂层为非晶态，有部分氮渗入铁素体中，导致材料脆性并降低瓷层与母材的结合强 度。焊接后热影响区内涂层晶化，形成AlO 、SiO晶体，使瓷层的耐蚀性降低。 2 3 2 关键词　搪瓷　涂层　晶体 An Investigation on the Interface between the Coating and Base Metal of　Welded Joints of Enamel Pipelines( Ⅱ) Wang Weidong　Wang Yong　He Yanling　Li honglin (University of Petroleum,Shandong) ［Abstract ］　An investigation on the welded enamel pipelines is taken via TEM in this paper. Before welded the enamel coating was of amorphous state, and some nitrogen atoms infiltrate in the ferrite of the matrix.This may cause the matrix brittle and may decrease the binding force between the coating and the matrix. After welded, the coating becomes crystal in HAZ , and Al O , SiO are formed. This may decrease the corrosion resistance of the 2 3 2 coating. Keywords　enamel　coating　crystal 1　前言 　　 钢管表面均匀地涂上一层搪瓷，将大大提高耐腐蚀性能，延长使用寿命。但长距 离油气管线需要将许多管线焊接起来。经过焊接以后，接头部位的喷瓷层将受到破 坏。而且由于喷瓷过程中需采用氮气保护，氮气会与焊条、搪瓷和母材一起参与热化 学反应，这样，不仅使接头成为管线耐腐蚀最薄弱的环节，而且由于氮的介入，导致 力学性能的下降。有关搪瓷与母材间的结合情况，涂层形貌受热循环影响的变化情 况，已在本文的第一部分作了介绍。这里对涂层与基体形成的相及其形态，进行了分 析，并提出解决这一问题的措施。 2　实验材料与样品制备 　　母材为φ158mm×6mm的Q235钢管，钢管端面开坡口，坡口角为60°。在氮气保 护下将管高频加热到700～900℃，在内外表面上喷以搪瓷釉料粉末。高温下粉末融 file:///E|/qk/clgc/clgc99/clgc9902/990208.htm（第 1／4 页）2010-3-22 16:17:13 材料工程990208 化，在钢管表面形成搪瓷层。釉料主要由AlO 、SiO 、MoO 、NaO、B O 及添加剂 2 3 2 3 2 2 3 组成。 　　采用对接接头，将喷好搪瓷的两段管线对焊起来。用直流焊机，反极性接法。焊 条为E4303וφ3.2，电流强度为110A，焊速约80mm/s。