稻壳粉废旧高密度聚乙烯复合材料的耐老化性能.pdfVIP

稻壳粉/废旧高密度聚乙烯复合材料的耐老化性能 卜凡华 王伟宏 王清文 （黑龙江省哈尔滨市东北林业大学生物质材料科学与技术教育部重点实验室 150040） 摘 要：主要研究了稻壳粉/废旧高密度聚乙烯（RH-HDPE ）复合材料在紫外加速老化和热氧老化条件下材 料性能的变化。实验结果表明紫外老化和热氧作用都使 RH-HDPE 复合材出现了褪色的现象；紫外老化使 材料的力学性能下降，而热氧作用使材料的弯曲强度增大。光稳定剂、紫外吸收剂和铁红都能够减少 RH-HDPE 复合材表面褪色和力学性能变化的程度，提高 WPC 的耐老化性能，三者同时加入具有协同作用。 关键词：废旧聚乙烯 稻壳粉 复合材料 老化 The stability of rice-hull-powder / recycled HDPE composites Bu Fanhua, Wang Weihong, Wang Qingwen, Dong Kangxu (Key Laboratory of Bio-based Material Science and Technology of Ministry of Education, Northeast Forestry University, Harbin 150040) Abstract: This paper studied the changes in the properties of rice -hull-powder/ high density polyethylene (RH/HDPE) composite after experiencing accelerate UV aging and thermal-oxidative aging. The results show that : UV irradiation and thermal-oxidative made RH-HDPE composite light; UV irradiation decreased the flexural properties of RH-HDPE composite, while thermal-oxidative improved the bending strength of RH-HDPE composite. Photostabilizer, UV absorbent, and iron oxide red can reduce fading and the extent changes in mechanical properties and enhance the anti-aging properties of WPC, when three additives were used together had a synergistic effect.. Keywords: Recyceled polyethylene, Rice hull powder, Composite, Aging 木塑复合材料（wood-plastics composites ，简称WPC ）是由一种或多种纤维素材料和一 种或多种热塑性塑料经由塑料加工工艺复合加工或进一步加工而成的材料或产品[1]，是循环 利用废弃塑料的一种良好途径。这种材料在尺寸稳定性、成型性、抗张力和抗冲击方面均具 有优势，尤其以良好的环保性能而受到国际上的普遍关注。除木材原料外，木塑行业还在积 极开发其他生物质纤维填充的塑料复合材料，其中稻壳粉已经得到大量应用。但在户外应用 中，木塑制品暴露在阳光和水分等环境下，制品颜色褪色和机械性能下降，每年造成百万美 元的损失，因此木塑复合材料的耐久性问题受到越来越多的关注[2]-[5] 。 我国木塑复合材料耐老性的研究远滞后于北美和欧洲，尤其是对废旧塑料为原料的木塑 复合材耐老化的研究我国近乎空白，这大大限制了木塑复合材料在我国的发展和在高新领域 的推广应用。为了进一步评定木塑复合的耐老化性能和开发新耐老化材料配方。本实验主要 研究了添加不同助剂的稻壳粉/废旧高密度聚乙烯复合材料在人工加速老化（热氧老化和紫 外老化）试验条件下的性能变化，从而总结出不同环境因素对材料老