技术研发 粉末涂料用GMA型丙烯酸树脂的 合成及其固化分析 □ 徐春雷,周正发,徐卫兵,任凤梅,欧阳彦辉 (合肥工业大学高分子科学与工程系,合肥 230009) 摘要：利用甲基丙烯酸甲酯、甲基丙烯酸缩水甘油酯(GMA)、丙烯酸丁酯进行自由基聚合合成GMA 型丙烯酸树脂。研究固化剂十二烷基二元酸用量、固化时间、固化温度、升温速率对涂层性能及固化 过程的影响。结果表明树脂与固化剂用量比为10∶2,固化条件为160 ℃固化30 min,制备的丙烯酸粉末 涂料具有良好的性能。 关键词：丙烯酸树脂；GMA；粉末涂料；固化剂 + 中图分类号：TQ630.4 1 文献标识码：A 文章编号：1006-2556(2008)02-0036-03 Analysis on the synthesis and curing of GMA type acrylic resin for powder coatings Xu Chunlei, Zhou Zhengfa, Xu Weibing, Ren Fengmei, Ouyang Yanhui (Department of Polymer Science and Engineering, Hefei University of Technology, Hefei 230009, Anhui Province) Abstract: We have prepared GMA-type acrylic resin through the radical polymerization of methyl methacrylate, glycidyl methacrylate, butyl acrylate and have studied the infl uence of dosage of dodecyl dibasic acid, curing time, curing time, curing temperature and heating rate on fi lm performance and curing process. The conclusions is got that acrylic powder coatings with good performance can be obtained under the conditions of resin and curing agent ratio 10:2 and 160℃, curing 30min. Keywords: acrylic resin, powder coatings, curing agent 0 前 言 1.2 树脂合成 GMA型丙烯酸树脂制成的粉末涂料保光保色 在装有温度计、搅拌器、回流冷凝管、滴加装 性好,耐候性极佳,适用于户外高装饰性涂装；耐热 置和氮气通入管的烧瓶中加入溶剂甲苯,过氧化苯 性好,不易变黄；附着力好,不需底漆；耐化学品性 甲酰为引发剂,用溶液法进行甲基丙烯酸甲酯、丙 好；物理机械性能好；静电涂装效果好,可薄涂等 烯酸丁酯、苯乙烯和GMA的自由基共聚反应。按 一系列优点,近年来成为丙烯酸类粉末涂料研究的 配方将原料单体和引发剂混合均匀,匀速滴加到温 热点[1-3]。本文利用甲基丙烯酸甲酯、甲基丙烯酸 度已经恒定的烧瓶中。反应结束后,得到均匀透明 缩水甘油酯、丙烯酸丁酯、苯乙烯进行自由基聚合 或者带有淡黄色的树脂溶液,经旋转蒸发、真空干 合成GMA型丙烯酸树脂,研究固化剂用量、固化时 燥脱除溶剂甲苯,即制得GMA型丙烯酸树脂。 间、固化温度、升温速率对涂层的影响,制备的丙 1.3 样板制备 烯酸粉末