MgO_Al_2O_3_SiO_2微晶玻璃析晶影响因素.pdfVIP

2 / 2007 10 MgO-Al O- SiO 2 3 2 T he Influence Factors of the Crystal Separating of MgO-Al O-SiO 2 3 2 Glass-ceramics , , , ( , 10073) YANG Juan, DU Yong-guo, LI Xiao-dong, ZHOU Wen-yuan ( Department of M aterial Engineering and Applied Chemistry, N ational U niversity of Defense Technology, Changsha 10073, China) : DSC M gO-Al O-SiO , 2 3 2 MgO-Al O -SiO : Mg2+ 2 3 2 , ( LT CC) : MAS; ; DSC; LT CC + + : TM 281; T Q171.71 8; T Q 171. 73 3 : A : 1001- 381( 2007) 10-00 2-03 Abstract: T he DSC technology w as used to investigate the affecting factors for the crystal separating of the MgO-Al2 O3-SiO2 glass-ceramics, including the component of material, the melting temperature of glass and the material state. T he factors benefit to the low temperature sintering of the glass- ce- ramic include the relative high content of Mg2+ , relative low melting temperature and the pow der state w ith many flaw s. T hese factors make it possible to be used as the low temperature co-fired ceramic substrate. Key words: MAS; glass- ceramics; DSC; LTCC , MAS 10Lm[ 1- 3] 1 ( LT CC, 1 , Low T emperature Co-fired Ceramic) , [ , 5] # ; 3 , 1500, 1520 e