核电站海工构筑物的防腐的研究.pdfVIP

The 6th China Corrosion Conference Corrosion Prevention Study of Marine Structures in Nuclear Power Station Gang SHEN, Peipeng QIAO Suzhou Nuclear Power Research institute ，Su Zhou,China,215004 Email: Heizi1982003@ Abstract: Marine Structures such as pumping stations, corridors, tunnels, water intake are the important part of the secondary circuit in nuclear power station .However, the risk of failure is very Serious and the design or maintenance face great challenges because of the marine environment. Crack, flack, damage, missing ribs and other issues was found in the nuclear power station commercial operation lass than 10 years. How to ensure the safety and effectiveness of the marine structures has become a urgent problem. Keywords: nuclear power station; marine structures; corrosion prevention 核电站海工构筑物的防腐研究 申罡，乔培鹏 苏州热工研究院电站寿命管理研究中心，苏州, 中国，215004 Email: Heizi1982003@ 摘 要：海工构筑物如泵房、廊道、隧道、取水口等对核电站的运行、安全和功能起到了极其重要的 作用，是核电站二回路的重要组成部分。但由于长期面临强腐蚀性的海水环境，失效风险非常大，防 腐设计和维修面临极大的挑战。国内某核电站在商运不到 10 年内便发现其联合泵房墙面出现裂缝、 砼脱落、破损、漏筋等一系列问题，严重危及核电站的正常运行，造成的大修和维修的成本高达数百 万。如何在工程阶段施加合适的防腐措施保证海工构筑物在商运期间的安全性和有效性，成为目前所 急需解决的问题。 关键词：核电站；海工构筑物；防腐 1 引言 核电站海工构筑物地处近海或海洋环境，按照 CCES 01-2004 《混凝土结构耐久性设计与施工指南》的 等级划分，环境类别处于D 级（严重）以上，腐蚀环境 极为恶劣。某核电站对泵房/燃料厂房/核辅助厂房等海 工构筑物进行混凝土结构进行评估，发现混凝土墙面出 Figure 1.Corrosion styles in nuclear power station 现裂缝、油漆破损、嵌缝材料脱落、堵洞材料和止水带 图1. 某核电站PX 泵房混凝土腐蚀缺陷 损坏等缺陷，如图1 所示，这些缺陷部分带有渗水和渗 漏现象，其中泵房的腐蚀情况已经危害其安全运行，造 成的停工和维修成本高达数百万。因此，熟悉核电站海 2.1 碳化 工构筑物的主要腐蚀类型，汲取国内外核电站或海洋环