Trans. Nonferrous Met. Soc. China 25(2015) 1011−1019 Interaction between AE44 magnesium alloy and SiC−Al O −SiO ceramic foam 2 3 2 1 2 1 Matej STEINACHER , Primož MRVAR , Franc ZUPANIČ 1. Faculty of Mechanical Engineering, University of Maribor, Smetanova ulica 17, SI-2000 Maribor, Slovenia; 2. Faculty of Natural Sciences and Engineering, University of Ljubljana, Aškerčeva cesta 12, SI-1000 Ljubljana, Slovenia Received 5 May 2014; accepted 8 October 2014 Abstract: The interaction between a molten magnesium alloy AE44 and a SiC−Al O −SiO ceramics and the resulting reaction 2 3 2 products were studied. The samples were investigated using optical and electron microscopy, energy dispersive X-ray spectroscopy and X-ray diffraction. SiO2 was predominantly reduced by Mg during the contact of the magnesium-rich melt with the ceramics. The main reaction product was MgO, whilst Si dissolved in the melt. Two novel tetragonal phases formed at the interface: AlSiRE and AlMgSiRE, having a specific mutual crystallographic orientation relationship. The interactions resulted in strongly connected interfaces between the metal and ceramics after short interaction time; however, interactions lead to disintegration of the ceramics after longer contact time. Key words: metal matrix composites; AE44 Mg alloy; ceramics; interfacial reaction