AISI 316不锈钢和Ti6Al4V合金在海水环境中的腐蚀与腐蚀磨损行为（英文版）.pdfVIP

Trans. Nonferrous Met. Soc. China 24(2014) 1022−1031 Corrosion and tribocorrosion behaviors of AISI 316 stainless steel and Ti6Al4V alloys in artificial seawater 1,2 1 1 1 2 Jun CHEN , Qing ZHANG , Quan-an LI , San-ling FU , Jian-zhang WANG 1. School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang 471023, China; 2. State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000, China Received 20 March 2013; accepted 3 January 2014 Abstract: The corrosion and tribocorrosion behaviors of AISI 316 stainless steel and Ti6Al4V alloys sliding against Al O in 2 3 artificial seawater using a pin-on-disk test rig were investigated. And the synergistic effect between corrosion and wear was emphatically evaluated. The results show that the open circuit potentials of both alloys drop down to more negative value due to friction. The corrosion current densities obtained under tribocorrosion condition are much higher than those under corrosion-only condition. Friction obviously accelerates the corrosion of the alloys. The wear loss for both alloys is larger in seawater than that in pure water. Wear loss is obviously accelerated by corrosion. And AISI 316 stainless steel is less resistant to sliding damage than Ti6Al4V alloy. The synergistic effect between wear and corros