Al410Cu142Mg057Mn012Zr合金热变形过程中显微组织动态演化的表征（英文版）.pdfVIP

Trans. Nonferrous Met. Soc. China 24(2014) 3477−3485 Characterization of dynamic microstructure evolution during hot deformation of Al−4.10Cu−1.42Mg−0.57Mn−0.12Zr alloy Can LIU1, Hui ZHANG1,2, Fu-lin JIANG1,3 1. College of Materials Science and Engineering, Hunan University, Changsha 410082, China; 2. Hunan Provincal Key Laboratory of Spray Deposition Technology and Application, Hunan University, Changsha 410082, China; 3. Department of Materials Science and Engineering, McMaster University, Hamiltion, Ontario L8S 4L7, Canada Received 6 January 2014; accepted 14 May 2014 Abstract: The Al−4.10Cu−1.42Mg−0.57Mn−0.12Zr alloy was compressed to different strains at deformation temperature of 300 ºC and strain rate of 10 s−1 on Gleeble−1500 system. The dynamic complex microstructures evolutions were investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The true stress−true strain curves exhibited a peak stress at critical strain, after which the flow stresses decreased monotonically, showing a dynamic flow softening. As the strain increased, the dislocation tangled to cell structure and sub-grain structure, which indicated the occurrence of dynamic recovery during deformation. Dynamic precipitations of S (Al CuMg), θ (Al Cu) and Al Zr phase were accelerated and coarsened by 2 2 3 deformation. Continuous S phases precipitated in the Al matrix and discontinuous S phases were found to be nucleated near the Al3Zr phase and at the