不同表面处理对灰铸铁摩擦学性能的影响.pdfVIP

不同表面处理对灰铸铁摩擦学性能的影响 史正良 潘健 （珠海格力电器股份有限公司机电技术研究院） 摘 要：灰铸铁是压缩机泵体常用材料，本文分别对灰铸铁样件进行磷化处理、磷化+纳米铁 离子表面处理、磷化+二硫化钼粘结固体涂层处理 ，在浸油润滑条件下，采用万能摩擦验机 ， 考察了灰铸铁在不同表面处理下的摩擦磨损性能。试验结果表明 ，磷化+二硫化钼粘结固体涂 层的摩擦系数最低，稳定在0.125 左右，并出现少量的粘着和磨粒磨损。 关键词：灰铸铁 表面处理 摩擦磨损 Effect of surface treatment on tribological behavior of gray cast iron Shi Zhengliang Pan Jian Abstract: The gray cast iron was common material used in compressor pump. Surface treatment such as Phosphate treatment, phosphate /Nano plasma surface treatment, phosphate / molybdenum disulfide coating were carried out on gray cast iron, surveyed the friction and wear property of iron cast iron with different surface treatment using mmw- 1 tribology testing machine under bath lubrication mode. Results showed that the sliding friction coefficient of phosphate / molybdenum disulfide coating was lower than the other two, the value stabilized at around 0.125, and appeared a small amount of adhesive and abrasive wear. Keywords: Gray Cast Iron, Surface Treatment, Friction and Wear 0 前言 灰铸铁具有一定的力学性能，优良的铸造性、加工性；由于基体中的富碳以石墨形式存 在，使其又具有优良的减磨性。因此，滚动转子式压缩机的曲轴广泛采用铸铁材料。压缩机 的曲轴传递电机扭矩，通过偏心曲轴压缩制冷剂气体，其反作用力将曲轴推向上、下轴承， 形成很大的接触压力。为隔离金属间的直接接触，避免运行中的咬死和烧伤，同时也为减小 【】 1 功耗，降低磨损，提高压缩机的可靠性，最常用的方法是磷化处理 。为了进一步提高涂层 的应用效果，本文分别对灰铸铁样件进行磷化处理、磷化+纳米铁离子表面处理、磷化+二硫 化钼涂层处理，考察了不同表面处理后的摩擦磨损性能。  史正良，1983 年2 月，珠海格力电器股份有限公司，研究员，szl0220@163.com Compressor and Motor Institute of Gree Electric Appliances, Inc. of Zhuhai 1 试验部分 1.1 磷化 磷化液成分不同，处理后的磷化膜的形态各不相同，本文使用的是锰系磷化液。磷化工 艺：试件上料→脱脂处理→水洗→表调 （浸入式）→磷化 （97℃浸入式）→ 清洗→烘干→抛 光。磷化膜均匀细小，完整致密，晶体密集堆积呈柱状结构。膜的主要成分是Mn (PO ) ·2MnH