热氧化对有热解碳界面层的SiCfSiC复合材料吸波和力学性能的影响.pdfVIP

Trans. Nonferrous Met. Soc. China 25(2015) 1484−1489 Effects of thermal oxidation on microwave-absorbing and mechanical properties of SiCf/SiC composites with PyC interphase 1 1 1,2 1 1 1 Yi-min SHI , Fa LUO , Dong-hai DING , Yang MU , Wan-cheng ZHOU , Dong-mei ZHU 1. State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China; 2. College of Materials and Mineral Resources, Xi’an University of Architecture and Technology, Xi’an 710055, China Received 16 June 2014; accepted 29 October 2014 Abstract: The SiC /SiC composites containing PyC interphase were prepared by chemical vapor infiltration process. The influences f of thermal oxidation on the complex permittivity and microwave absorption properties of SiCf/SiC composites were investigated in the frequency range of 8.2−12.4 GHz. Both the real and imaginary parts of the complex permittivity decreased after thermal oxidation. The composites after 100 h thermal oxidation showed that reflection loss exceeded −10 dB in the frequency of 9.7−11.9 GHz and the minimum value was −11.4 dB at 11.0 GHz. The flexural strength of composites decreased but fracture behavior was improved obviously after thermal oxidation. These results indicate that the SiCf/SiC composites containing PyC interphase after thermal oxidation possess good microwave absorbing property and fracture behavior. Key words: SiCf/SiC composites; thermal oxidation; dielectric properties; microwave absorbing; mechanical properties behavior through