金属薄板直壁件数字化渐进成形过程的实验研究.pdfVIP

　　锻压技术 　2004 年 　第 6 期 金属薄板直壁件数字化渐进成形过程的实验研究 王 　莉 　莫健华 　黄树槐 (华中科技大学模具技术国家重点实验室 　430074) 　　摘要 : 金属薄板直壁件的成形是数字化渐进成形技术中的热点和难点之一。本文基于数字化渐 进成形的基本原理提出了一种加工金属直壁件的方法 , 在实验中研究金属薄板直壁件的成形过程 , 了解直壁成形机理和控制成形过程的工艺措施。 关键词 : 金属板料数字化成形 　渐进成形 　直壁件 Experimental study of straightwall parts forming process based on sheet metal digital incremental forming WANGLi 　MO Jianhua 　HUANG Shuhuai ( State Key Laboratory of Die Mould Technology , Huazhong University of Science and Technology) Abstract : It is a key and difficult point for sheet metal digital incremental forming to produce straightwall parts direct 　　 ly. According to the general mechanism of sheet metal digital incremental forming , a method is introduced to form the straightwall parts successfully. In this paper , the straightwall parts ’forming process is studied by means of experiments , in order to know how the straightwall is formed and how to control the forming process. Keywords : Sheet metal digital incremental forming 　Incremental forming 　Straightwall parts 一、引言 二、成形机理分析 金属薄板的数字化渐进成形技术是一种近几年 为使问题简化 , 以轴对称零件为对象, 引入柱 来国际上刚刚开始研究的新型板材加工工艺。它采 面坐标 , (见图 1a) 其中 z 轴表示板厚方向, r 和 θ 用快速成形制造技术中“分层制造”的思想 , 着重 分别表示径向和周向。分别讨论一次成形的一般情 强调“层”作为加工单元的特点 , 将三维形状加工 况及直壁成形。 分解成一系列二维层上的塑性加工。在加工中发现 , 尽管用该技术可准确迅速地制成大量复杂形状的金 属薄板零件 , 但对于具有直壁特征的零件几乎无法 一次成形。对板厚为 1mm 的 08Al 钢板进行直接成 形直壁的实验中发现 , 可成形的直壁高度极限值为 125mm 。基于数字化渐进成形技术加工金属直壁 件的成形方法 , 以方盒形直壁件的成形为例, 在实 图 1 　一次成形时变形模式图 验中了解其变形过程和控制成形的工艺措施。 1 一次成形的一般情况 加工第 1 层时 , 压头与水平面内铺放的板料相