本钢薄板坯连铸机生产无取向硅钢工艺研究.pdfVIP

本钢薄板坯连铸机生产无取向硅钢工艺研究 1 李明光 李秉强 于华财 林东 （本钢炼钢厂，辽宁本溪 117000 ） 摘要：主要描述了本钢采用 FTSC 薄板坯连铸机生产无取向硅钢的生产实践，优化出了最佳的 LF+RH 精炼工 艺路线，稳定地控制了钢中的[C]、[Si]、[N]、等难控元素，提高了钢水的纯净度，钢水的可浇性好，实现多炉 连浇。 关键词；FTSC 薄板坯；工艺优化；成分控制；连铸可浇性 THE TECHNOLOGY STUDY OF NON- ORIENTED SILICON STEEL AT THIN SLAB CASTER IN BENXI-STEEL LI Mingguang, LI Bingqiang, YU Huacai, LIN Dong （BenXi-Steel steel-making Plant, BenXi, Liaoning 117000, China ） Abstract: This paper mainly describes the production practice of si-steel at thin slab caster in Bengang. The best process routes with LF+RH has been optimized, and the elements in steel such as [C]、[SI]、[N] etc. which are difficult controlled have been controlled stably, therefore, the steel cleanliness is improved , the castability of steel is good and continuous casting with multiple heats is realized. Keywords: Thin slab casting, process optimization, [C] 、[N]、[Si] composition control, castability 为了充分发挥本钢 FTSC 薄板坯生产线优势，加快产品结构调整，扩大品种规模和比例，2007 年初 开始，本钢组织广大技术人员对 FTSC 薄板坯铸机生产超低碳钢汽车板用钢进行研究与开发，经半年多 的生产实践，对薄坯连铸机生产超低碳汽车板用钢取得了一定的成绩。采用 FTSC 薄板坯铸机生产硅钢 虽起步较晚，但借鉴超低碳汽车板用钢的生产工艺，使本钢在硅钢的生产中生产工艺取得了重大的突破， 在不对钢水进行钙处理的情况下，实现了连浇 4 炉以上，且硅钢成分均控制在内控范围内。 1 本钢FTSC 薄板坯连铸连轧硅钢工艺流程 高炉铁水—150 复吹转炉—LF+RH/TB 精炼—FTSC 薄板坯连铸机—辊道式加热炉—六机架轧机—板 卷。其中，供 FTSC 薄板生产线配备：2 座 150 吨转炉，2 台LF 钢包炉，1 台双工位RH/TB，2 台FTSC 薄板坯连铸机，2 条辊道式保温加热炉，1 台 7 架轧机。 作者简介：李明光，男，学士，工程师，钢铁冶金专业。 1200 2 硅钢设计的化学成分要求及实际冶炼成分 表 1 为硅钢的牌号及设计成分要求，表 2 为实际冶炼的硅钢成分。 表1 硅钢成分要求 %/ 牌号 标准 C Si Mn P S 50BW600 企标 ≤0.008 1.00～1.30 0.10～0.30 ≤0.030 ≤0.008 内控