铁氧体参数及国内外牌号对照表.docVIP

HARD FERRITE MAGNETS?? Hard ferrite (ceramic) magnets were developed in the 1960s as a low cost alternative to metallic magnets. Even though they exhibit low energy (compared with other permanent magnet materials) and are relatively brittle and hard, ferrite magnets have won wide acceptance due to their good resistance to demagnetization, excellent corrosion resistance and low price per pound. In fact, measured by weight, ferrite represents more than 75 percent of the world magnet consumption. It is the first choice for most types of DC motors, magnetic separators, magnetic resonance imaging and automotive sensors.??? ? Ferrite Magnets characteristics Mostly Used national standard - SJ285-77 permanent ferrite magnet standard Grade Value(min/typical in our factory) Br Hcb(BHC) Hcj(IHC) (BH)max MT KG KA/m Koe KA/m KOe Kj/m^3 MGOe Y10T(=C1) 200/218 2.00/2.18 125/145 1.57/1.82 210/250 2.64/3.14 6.5/8.0 0.8/1.0 Y25 360/370 3.60/3.70 135/150 1.70/1.88 140/170 1.76/2.14 22.5/25.3 2.8/3.2 Y30(=C5) 380/385 3.80/3.85 191/210 2.40/2.64 199/220 2.50/2.51 26.0/28 3.4/3.7 Y30BH 380/390 3.80/3.90 223/235 2.80/2.95 231/245 2.90/3.08 27.0/30.0 3.4/3.7 Y33 410/420 4.10/4.20 220/235 2.77/2.95 225/240 2.83/3.01 31.5/33.0 4.0/4.2 Y35 400/410 4.00/4.10 175/195 2.20/2.45 180/200 2.26/2.51 30.0/32.0 3.8/4.0 C8(=C8A) 385/390 3.85/3.90 235/255 2.95/3.20 242/265 3.05/3.33 27.8/30.0 3.5/3.7 C10 400/410 4.00/4.10 288/300 3.62/3.77 280/287 3.51/3.60 30.4/31.9 3.8/4.0 　 Chinese SJ/T0410-2000 Permanent Ferrite Manget Standard Grade BR HcB HcJ (BH)max mT KG KA/m Koe KA/m Koe Kj/m MGOe Y8T 200～235 2.0～2.35 125～160 1.57～2.01 210～280 2.64～3.52 6.5～9.5 0.8～1.2 Y20 320～380 3.2～3.8 135～190 1.70～2.38 140～195 1.76～2.45 18.0～22.0 2.3～2.8 Y22H 310～360 3.1～3.6 220～250 2.77～3.14 280～320 3.52～4.02 20.0～24.0 2.5～3.0 Y23 320～370 3.2～3.7 170～190 2.14～2.38 190～230 2.39～2.89