三维自组装膜的制备及其摩擦磨损试验.pdf

三维自组装膜的制备及其摩擦磨损试验 徐中。王磊 (大连理工大学，大连116024) 料。为便于自组装，利用高分子网络凝胶法的空间限域作用制备单分散性PET／高岭土复合微球，并利用改进的 验法研究了微球平均粒径、超声振荡功率、反应温度与微球质量分数对薄膜表面粗糙度、摩擦系数的影响。采用动 摩擦系数精密测定装置评价自组装薄膜同钢对磨时的摩擦磨损性能。薄膜表面摩擦系数(0．09～o．16)明显低于 无膜基片表面摩擦系数(0．78)，表明该自组装膜在低栽荷下具有较好的减摩性能。 [关键词] 自组装；摩擦磨损；正交实验；非光滑表面；薄膜 [中图分类号-]TGl74．42 [文献标识码]A and BehaviorofaSelf-assembledFilm PreparationTribological withBionicNonsmoothedSurface Lei xuZhong，WANG (Dalian of 1 16024，China) UniversityTechnology，Dalian Atfirst．kaolinwasmodified sulfoxide(DMSO)．PET／kaolinmicro— [Abstract] byusingdimethyl composite with network filmuniformdistributionmicro- were gelmethod．IPN／PET／kaolincomposite spheresproducedpolymer sizedconvex were influenceon hull／pit preparedbyimprovedevaporation—induced thefrictionfactorandRaoftheself—assembledfilm diameterof byaverage composite power， wereresearched method．Coefficient0fkineticfric—tion meas— reac—tion precision temperature byorthogonalexperiment film coefficientofthefilmsur— devicewasusedtoevaluatefrictionandwear betweenandmetal．Friction uring properties lowerthanthatofthesurfacewithoutthefilm(0．78)．Theresultsshowthattheself— faee(0．09～0．16)was obviously assembledfilmhasanexcellentantifriction ability．