《金属间化合物对钛合金与不锈钢的热轧焊过渡接头耐热性的影响(英文期刊)》.pdfVIP

Trans. Nonferrous Met. Soc. China 23(2013) 1966− 1970 Effect of intermetallic compounds on heat resistance of hot roll bonded titanium alloy−stainless steel transition joint 1 2 1 Dong-sheng ZHAO , Jiu-chun YAN , Yu-jun LIU 1. State Key Laboratory of Structural Analysis for Industrial Equipment, School of Naval Architecture, Dalian University of Technology, Dalian 116024, China; 2. State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China Received 20 June 2012; accepted 17 September 2012 Abstract: The effect of intermetallic compounds on the heat resistance of transition joint was investigated. The experiment of post-weld heat treatment for the hot roll bonded titanium alloy−stainless steel joint using nickels interlayer was carried out, and the interface microstructure evolution due to heat treatment was presented. There was not found significant interdiffusion at stainless steel/nickel interface, when the specimens were heat treated in the temperature range of 600−800 °C for 10 and 30 min, while micro-cracks occurred at the stainless steel/nickel interface heat treated at 700 °C for 30 min. The thickness of intermetallic layers at nickel/titanium alloy interface increased at 600 °C, and micro-cracks occurred at 700 and 800 °C. The micro-cracks occurred between intermetallic layers or between intermetallic layer and nickel interlayer as well. The tensile strength of the transition joint decreased with the increase of heat treatment temperature or holding time. Key