《均匀化处理对含钪AlZnMgZr合金组织的影响(英文期刊)》.pdfVIP

Trans. Nonferrous Met. Soc. China 23(2013) 3568−3574 Microstructural evolution of Al−Zn−Mg−Zr alloy with trace amount of Sc during homogenization treatment 1 1,2 1 1 1 Bo LI , Qing-lin PAN , Yun-jia SHI , Chen LI , Zhi-min YIN 1. School of Materials Science and Engineering, Central South University, Changsha 410083, China; 2. Key Laboratory of Nonferrous Materials Science and Engineering of Ministry of Education, Central South University, Changsha 410083, China Received 20 July 2013; accepted 25 October 2013 Abstract: The microstructural evolution of Al−Zn−Mg−Zr alloy with trace amount of Sc during homogenization treatment was studied by means of metallographic analysis, scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and differential scanning calorimetry (DSC). The results show that serious dendritic segregation exists in studied alloy ingot. There are many eutectic phases with low melting-point at grain boundary and the distribution of main elements along interdendritic region varies periodically. Elements Zn, Mg and Cu distribute unevenly from grain boundary to the inside of alloy. With increasing the homogenization temperature or prolonging the holding time, the residual phases are dissolved into matrix α(Al) gradually during homogenization treatment, all elements become more homogenized. The overburnt temperature of studied alloy is 476.7 °C. When homogenization temperature increases to 480 °C, some spherical phases and redissolved triangular constituents at