《工业AA1200铝合金薄板拉伸成形模拟和实验研究（英文版）》.pdfVIP

Trans. Nonferrous Met. Soc. China 24(2014) 484−490 Simulated and experimental investigation of stretch sheet forming of commercial AA1200 aluminum alloy Reza ESMAEILIZADEH1 1 2 3 , Kourosh KHALILI , Bagher MOHAMMADSADEGHI , Hossein ARABI 1. Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran; 2. School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Narmak, Tehran, Iran; 3. Center of Excellence for High Strength Alloy Technology, School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Narmak, Tehran, Iran Received 18 June 2013; accepted 24 September 2013 Abstract: The simulation and experimental results obtained from stretching test of a commercial sheet of AA 1200 aluminum alloy were compared and evaluated. Uniaxial tensile tests were carried out to obtain the required input parameters for simulation. Finite element analysis of the forming process was carried out using Abaqus/Explicit by considering von Mises and Hill-1948 yield criteria. Simulation results including punch force and strain distribution were compared and validated with the experimental results. The results reveal that using anisotropic yield criteria for simulation has a better match in both cases with the experiments. Key words: AA1200 aluminum alloy; sheet forming; stretch forming; numerical simulation; yield criteria Stretching is common in stamping. This property 1 Introduction