《轧制对Mg3Cu1Mn合金温度阻尼峰的影响(英文期刊)》.pdfVIP

Trans. Nonferrous Met. Soc. China 23(2013) 1610−1616 Influence of rolling on internal friction peak of Mg−3Cu−1Mn alloy Hai ZHOU1,2, Jing-feng WANG1,2, Fu-sheng PAN1,2, Dan-dan XU1,2, Ai-tao TANG1,2, Hao LIANG3 1. National Engineering Research Center for MagnesiumAlloys, Chongqing University, Chongqing 400044, China; 2. College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China; 3. Institute of System Engineering, China Academy of Engineering Physics, Mianyang 621900, China Received 13 February 2012; accepted 15 June 2013 Abstract: The damping capacities of as-rolled Mg−3Cu−1Mn (CM31) alloy were studied by dynamic mechanical analyses. The internal friction in the first heating shows peaks P , P and P at 118, 190, and 320 °C, respectively. The significant peak P , which 1 2 3 3 can not be found in the cast CM31 alloy, appears in the first heating Q−1 −1 curve and disappears in the second heating Q curve. The influence of rolling on the internal friction peaks of the CM31 alloy was investigated by optical microscopy, X-ray diffraction, and electron backscatter diffraction analyses. The results show that the textures are enhanced and the twins rapidly disappear while peak P3 appears after deformation of the CM31 alloy, and confirm that the three internal friction peaks are the dislocation damping peak, grain boundary damping peak, and the recrystallization peak caused by twins, in the as-rolled CM31 alloy. Key words: rolling; magnesium alloys CM31; twinning; in