年产25000吨镁砖生产车间设计毕业论文.docVIP

年产25000吨镁砖生产车间设计 摘要 关键词： The Design Of Workshop for Producing 25000 Tons Magnesia Brick Per Year Abstract Our country is famous in the world for abundant resources of high-quality magnesite. The broad coastline and salt lake in our country provide the bright prospect to extract magnesia too. Nature-endowed conditions are offered for the development of magnesia based refractories in our country. Magnesia based refractories consist of MgO as the primary chemical constituent with the primary phases of periclase. At present, main products of magnesia based refractories include normal magnesia brick, direct-bonding magnesia brick, magnesia-calcia brick, magnesia-silica brick, magnesia-alumina brick, magnesia-chrome brick and magnesia-carbon brick. In addition, there are other type of magnesia based refractories which are free of firing and various unshaped products. Normal magnesia brick is made from sintered magnesia and then fired at high temperatures, which contains about 91% MgO with the silicate as the bonding phases. Direct bonding magnesia brick contains more than 95% MgO, in which the grains is bonded together with each other by high temperature sintering. This work designs a plant for producing MZ-91 normal magnesia brick of 10000 tons per year and direct bonding MZ-95 magnesia brick of 15000 tons per year. The application conditions and processing fundamentals for magnesia brick are reviewed. Requirements for raw materials, processing technique, process flow, balance calculation of raw-materials supply, selection of firing equipments and related calculation and the processing inspection system in the production sequence are clarified. Characteristic of this workshop design is elucidated. Keywords: Refractory; Magnesia brick; Processing, Workshop design; 目 录 摘 要 Ⅰ Abstract Ⅱ 1 绪论 1 1.1 镁砖的发展历史 1 1.2 镁砖的应用 2 2 工艺部分 3 2.1 工艺的理论基础 3 2.1.1 4 2.1.2 破粉碎 5 2.1.3 筛分 5 2.1.4 物料的贮存 5 2.1.5 配料 6 2.1.6 混练 6 2.1.7 成型 6 2.1.8 干燥 6 2.1.9 烧成 7 2.1.10 成品仓库