奥氏体不锈钢氢脆.pdfVIP

专 论 Monograph 奥氏体不锈钢氢脆 余存烨 (上海统谊石化设备检测有限公司，上海200540) 摘  要：本文论述了奥氏体不锈钢在化工环境与氢气环境中使用时发生的氢脆现象，氢脆对 应力腐蚀开裂有关系，分析了影响氢脆的各种因素，如马氏体相变、镍当量等，并讨论了不锈钢 氢脆机理。 关键词：不锈钢　氢脆　应力腐蚀破裂　马氏体 中图分类号： 文献标识码： DOI：10.13726/j .cnki.11-2706/tq.2015.08.011.05 TG17 A Hydrogen Environment on Austenite Stainless Steel YU Cun-ye (Shanghai Petrochemical Co., Ltd., Shanghai 200540, China) Abstract: In this article ，take place appearance of hydrogen environment on austenite stainless steel in chemical process environment and hydrogen gas were deseribed. Hydrogen environment related to stress corrosion cracking . Each factor of hydrogen environment, such as martensite phase transformation ，nickel equivalent etc were analyzed. And hydrogen mechanism on stainless steel were 术 技 discussed. Key words: stainless steel; hydrogen environment; stress corrosion cracking; martensite 0 引言 钢如超过NACE规定容许的硬度(HRC22)也会发生脆 长期以来工程上对奥氏体不锈钢(以下简称不锈 裂，即使在化工水溶液腐蚀环境下，不锈钢不是不 钢)氢脆(HE)常被忽视，而对其应力腐蚀破裂(SCC) 发生氢脆，尤其某些应力腐蚀开裂，更是由阴极氢 较为重视。不锈钢作为耐腐蚀材料，与碳钢、低合 致开裂引起的。 金钢比较难于发生由腐蚀引起的氢脆，但在高压氢 1 不锈钢氢脆事例 气环境下，金属材料多会发生氢脆，耐腐蚀性优异 的不锈钢也不例外，存在氢脆的危险。1960年代， 关于不锈钢氢脆事故，作者在上海石化曾参与 NASA 曾对氢储藏容器发生过的开裂事故加以总结， 分析过三例： 近年来由于以氢作新能源，氢电池汽车开发以及站 (1)芳烃厂制氢装置有两台石脑油蒸发器，材质 台配置供氢的储罐、配管和阀门等需不锈钢，因此 上部为13CrMo44 ，下部为1.454 1(0Cr 18Ni9Ti) 。介 对不锈钢高压氢气环境下氢脆研究成为热点。当 质管程为石脑油、氢气、壳程为转化气(水、蒸气、 然，在石化加氢