熟料粉颗粒级配对水泥性能影响的试验研究详解.docVIP

2014届毕业论文 熟料粉颗粒级配对水泥性能影响的 试验研究 院、 部：材料与化学工程学院 学生姓名 易成韬 指导教师：李坦平 职称 教授 专 业：无机非金属材料工程 班 级：材本1001班 完成时间： 2014年5月  摘 要 随着水泥行业的发展，以及新的国家标准的出台，公司生产的水泥细度较以前有了大的提高，现在P.O 32.5和P.O42.5水泥的比表面积普遍在350㎡/kg-380㎡/kg。熟料粉的颗粒级配也不是越小越好，当熟料的细度小到一定程度的时候，会对一些水泥性能产生影响。我们通过对熟料粉进行二次粉磨得到不同细度的熟料粉颗粒，再将不同细度的熟料粉与矿粉（365㎡ABSTRACT With the introduction of the development of the cement industry, as well as the new national standards, the fineness of the cement produced has greatly improved compared to the past, present and P.O42.5 PO 32.5 cement surface area of 350 m2 / kg-380 m2/ kg. Guessed powder particle size distribution is not as small as possible, fineness when Guessed small to a certain extent, will affect the performance of some cement. We got guessed powder particles of different fineness guessed by secondary grinding flour, then guessed different fineness powder and slag (365 m2/ kg), a certain proportion of gypsum powder obtained by mixing different uniform fineness of slag cement, and through a variety of experiments comparing the performance difference between different slag cement fineness. Experimental study of particle gradation guessed powder prepared by affecting its normal consistency of cement water, stability, setting time, mortar fluidity and strength development. Key words: guessed powder；particle size distribution；clotting time；mortar fluidity；strength 目 录 湖南工学院2014届毕业设计（论文）课题任务书 1 湖南工学院本科生毕业论文开题报告 3 湖南工学院毕业设计(论文)工作进度检查表 6 湖南工学院2014毕业设计（论文）指导教师评阅表 8 湖南工学院毕业设计（论文）评阅评语表 9 湖南工学院毕业设计（论文）答辩资格审查表 10 湖南工学院2014届毕业论文答辩及最终成绩评定表 12 1、绪论 13 1.1水泥在国民经济中的重要地位 13 1.2新型干法水泥生产技术的现状 13 1.2.1预分解窑煅烧工艺和技术装备的现状 13 1.2.2粉磨粉碎技术与装备 14 1.2.3信息化自动控制技术 15 1.3课题意义与研究目的 15 2、试验原材料和试验方法 16 2.1 试验原材料 16 2.2 试验步骤概要与水泥制备 16 2.2.1、试验步骤概要 16 2.2.2、水泥制备 16 2.3 试验步骤 17 2.3.1测定水泥比表面积 17 2.3.2检测水泥标准稠度用水量、凝结时间以及安定性 19 2.3.3检测水泥胶砂流动度 21 2.3.4检测水泥强度 22 3、实验结果与处理分析 25 3.1 熟料粉细度对水泥安定性以及凝结时间的影响 25 3.2 熟料粉细度对标准稠度用水量以及胶