7 湿纸页的传递.pptVIP

Wet Web Transfer 湿纸页的传递 Web transfer Wire to press section; one press to next one; press to dryer section. Web transfer: - open draw (web tension) - closed transfer (vacuum pickup) 湿纸页的传递 开式引纸 闭式引纸 粘舐引纸 真空引纸 开式引纸 人工引纸：手持一块半干纸料，将网部水针切下的湿纸条粘附在半干纸料上，迅速传到一压毛毯。开式引纸只靠湿纸本身的强度，而没有任何外界的支持，经引纸辊传递到一压毛毯上去。 压缩空气引纸：用压缩空气将湿纸页吹到引纸辊并传到毛毯。 开式引纸 Forming section 成形部 Press section 压榨部 Transfer pick up roll 引纸辊 Tri-nip press Open draw Forming section Transfer pick up roll Suction roll 引纸辊 成形部 开放式引纸 真空辊 湿纸剥离的机理 - Liquid film thickness between the web and roll (The work of adhesion increases with decreasing film thickness.) - Liquid cavitation (Microscopically sharp features in a roll exhibit excess surface energy and can serve as nucleating sites for many surface phenomena such as condensation, particle separation, and air bubble formation. All these can reduce adhesion and help web release.) - Surface energy (Surface energies of roll cover and sheet material are important factors in evaluation of wettability and release mechanisms.) 影响湿纸剥离的因素 - Furnish, fillers, fines - Temperature and pH - Surface roughness of a press roll - White water composition 剥离点：湿纸幅离开伏辊的位置。 剥离点位于真空伏辊的真空区，揭纸时可能受到很大的张力，容易引起湿纸的断头。但若湿纸幅经过真空区以后，进入眼孔中的水被离心力甩出的喷水区内，纸的水分增加，湿纸强度降低，也容易引起断头。 湿纸的剥离点应当在真空区以前和喷水区以前即B、C之间。通常剥离点应略微超过真空伏辊的真空室后方边缘。 湿纸页的受力分析 湿纸与造纸网间的粘着力 水的表面张力 离心力 湿纸重力 惯性力 张力 Mardon equation S——湿纸页的张力 (g/cm) W——剥离功(erg/cm2) 1erg=10-7J φ——剥离角，θ=π/2－φ m——单位面积纸页质量(g/cm2) V——纸页剥离速度(cm/s) 剥离角：伏辊在剥离点的切线与湿纸页的夹角。 一般长网纸机，剥离角为30°。增加剥离角，剥离功减小。 Why Closed Draw?封闭引纸原因 Closed draw offers 封闭引纸带来 low sensitivity to paper machine breaks 减少断头 best potential for furnish optimization良好浆料优化潜力 low solids high bulk operation低的干度和高的松厚度操作 stabile web handling for sheet edges 稳定的纸边处理 Web tension in an open draw开放引纸中纸页强度 湿纸页的剥离性能 剥离角与湿纸撕裂的关系 当?90°，湿纸在揭纸时出现撕裂，裂口将逐渐扩大。当?90°时，裂口会逐渐自行封闭，可以减少伏辊引纸的断头。 引纸辊的作用 一是保证湿纸页按照最优曲线运行减少张力。 二是控制湿纸幅，使其不在伏辊与一