薄板坯表面纵裂的成因及防止措施文稿.docVIP

第一篇 专题部分 薄板坯表面纵裂的成因及其防止措施 薄板坯表面纵裂的成因及防止措施 摘 要 对珠钢、包钢薄板坯表面纵裂进行分析后发现，产生薄板坯表面纵裂的主要原因有钢中含碳量、硫含量、结晶器热流密度、拉速。避免钢中含碳量在敏感区，控制热流密度在临界热流密度以下，选择合理拉速等对提高薄板坯质量，防止表面纵裂有重要作用。 关键词 连铸 表面纵裂 薄板坯 Abstract Surface longitudinal cracks on thin slabs which are produced by Zhujiang IronSteel Company and Baotou IronSteel Company are studied ,and find that there are several factors maybe lead to surface longitudinal cracks on thin slabs. Influences include carbon content ,sulfur content ,thermal energy density,pull speed ,etc .In order to improve the quantity of steel ,it should control