磷酸钙的溶胶凝胶制备法及应用重点.pptVIP

Contents Materials Research Bulletin 41 (2006) 1754–1762 Discussion: Fig6: SEM micrograph of HA powders derived from EDTA route. Discussion: Conclusion Fig8: A flow chart of the sol–gel synthesis of HA powder. Fig9:XRD pattern of the HA nanopowders sintered at 600 ℃. Fig10:Phase composition of the samples sintered at different temperatures 600 ?C, 700 ?C, 800 ?C and 900 ?C. Fig11:TEM micrograph of HA nanopowders sintered at 600 ℃. HA nanopowder with crystallites of 20–30nm size was prepared via a simple sol–gel method. Through appropriate sintering at temperature of 600 ?C, the