粒径与形状.pptxVIP

粉體粒徑分析;各種可能的性狀之粒子;取樣Sampling;Grab sample; cone quarter; Riffling 等三種實驗室方式取樣 From JS Reed, 2nd ed.;Sampling Accuracy;Two-Component Sampling Accuracy;各種粒徑的定義;各種粒徑的定義(2);* Martin diameter: 實際上可以選許多方向畫線, 然後平均之;From TA Ring, 1996.;Coulter counter: 每當一顆粒子通過aperature時會因為排開同體積導電溶液, 造成電阻上升效果, 所以可用於粒子計數, 以及定量其大小 問題: 一次多顆通過, 或多顆連續通過, 太大的太重的粒子, 會被電解的粒子, aperature被塞住等等;Microscopic Method;其他粒徑量測技術;Forward scatter, side scatter, back scatter;Some Terminology;PCS or DLS 基本上是量測粒子散射光的相對強度, 運動前後的差別, 利用correlator來分析數據, complex mathematics;Hydrodynamic Chromatography;Rf = (time of passage of marker)/ (time of passage of colloid) versus colloid size ? calibration ;X-ray Line Broadening;From JS Reed, 2nd ed. 好的儀器測量結果大致相仿, 但不易某方法一統江湖.;* From TA Ring, 1996; 量測誤差與所計粒子數目平方根成反比;Shape Factor;All particles are hydrous zinc oxide (from different precipitation conditions): Shapes are different;ψA/ψV ? index of angularity (shape factor based on area/shape factor based on volume);* 取自TA Ring, 1996; ?S/?V = St/V . Dav ; 其中St/V 表示單位粒子體積的表面積 (與單位重量表面積類似), 是一個容易量測的項目;More Shape Factors;Fractal Shapes;取自TA Ring, 1996;粒徑分布;Size 區分: linear or geometric 幾何級數, e.g. 2 ? ;粒徑分佈數學式;More Equations;From TA Ring, 1996; bimodal distribution 本圖示由兩種粒子混合得到, 若為單一粒子, 則可能表示合成過程有兩種不同的機制, 造成兩個粒徑分布;平均粒徑;凝聚體特性;In general: ? = ?o exp( - b ?); ?/?tho = 1 - ?;From Am. Cer. Soc. Bull., 65, 1591, 1986. 結論: 弱的凝聚體可以提供較佳的燒結密度 Soft agglomerate vs strong agglomerate;破壞凝聚體的一些方法