题 目 专 业 学生姓名 ╳╳╳ 学 号 指导教师 ╳╳╳ 论文字数 完成日期 201年月 摘 要热挤压就是将金属材料加热到热锻成形温度进行挤压，即在挤压前将坯料加热到金属的再结晶温度以上的某个温度下进行的挤压热挤压是几种挤压工艺中最早采用的挤压成形技术，它是在热锻温度下借助于材料塑性好的特点，对金属进行各种挤压成形。目前，热挤压主要用于制造普通等截面的长形件、型材、管材、棒材及各种机器零件等。热挤压不仅可以成形塑性好，强度相对较低的有色金属及其合金，低、中碳钢等，而且还可以成形强度较高的高碳、高合金钢，如结构用特殊、不锈钢、高速工具钢和耐热钢等。关键词 Abstract The hot extrusion of metal material is heated to the temperature of hot forging extrusion, namely before extrusion billet heating to metal extrusion of a recrystallization temperature above the temperature. Hot extrusion extrusion technology is the earliest use of the technology of extrusion several, it is by means of material characteristics of plastic in the hot forging temperature, the metal extrusion forming. At present, hot extrusion is mainly used in the manufacture of ordinary uniform long shaped parts, profiles, tubes, rods and various machine parts etc.. Hot extrusion can not only forming plastic, non-ferrous metal and alloy relatively low strength, low carbon steel, etc., but also can form high strength, high carbon high alloy steels, such as stainless steel, with special structure, high speed steel and heat resisting steel. Magnesium is with dense row of six square lattice metal, slip system is only 3, compared with aluminum, copper, plastic and magnesium is very low. Cold extrusion of magnesium is difficult, but is heated to 200 DEG C, plastic magnesium has been greatly improved, so the plastic processing of magnesium alloy is the use of hot extrusion forming. This paper considers the magnesium alloy ZK60 is heated to 330 degrees hot extrusion with high frequency heating. Keywords: magnesium alloy; hot extrusion; high-frequency heating mold; 目录 1章 绪论 1 1.1 热挤压概述 1 1.2 镁合金热挤压研究 第2章 设计内容 2.1 设计任务 2.2 设计要求 2.3 设计方案的构想 第3章 设计实现 3.1工况及要求 3.2 参数计算 参考文献 致 谢 。 附录 图纸列表 。 第1章 绪论 1.1热挤压概述 挤压模挤压安装在压力机，