东洋纺阻燃TPEE物性表.docVIP

Flame-resistance type Item Method Unit Flame-resistance type P50DFR S2002FB S2004FS Hardness JIS K6301 A 96 98 98 ASTM D2240 D 54 57 58 Specific Gravity ASTM D792 ? 1.36 1.33 1.28 50% Tensile Modulus ASTM D638 MPa 10.8 16.6 20.1 10% Compression Modulus ASTM D695 MPa 9.4 15.8 19.2 Flexual Modulus ASTM D790 MPa 167 230 290 Tensile Strength ASTM D638 MPa 17.6 26.9 27.2 Tensile elongation ASTM D638 % 600 560 550 Tear Strength ASTM D624 kN/m 108 160 155 IZOD notched impact test ASTM D256 J/m NB NB NB Taber abrasion ASTM D1044 mg/1000c. 17 12 12 Resilience JIS K6301 % 65 60 60 Compression set JIS K6301 % 55 65 65 Melting point DSC 215 210 210 Vicat Softening point ASTM D1525 170 185 185 Heat deflection temperature ASTM D648 70 110 110 Brittle point JIS K6301 -65 -65 -65 Flammability UL94 ? V0 V2 class V2 class Coefficient of heat expansion TMA 1/K 16×10-5 13×10-5 14×10-5 Dielectric strength JIS K2111 MV/m 15 25 30 Volume strength ASTM D257 Ω?cm 6×1013 4×1013 2×1013 Moisture absorption 23,65%RH % 0.40 0.38 0.38 Melt flow index ASTM D1238 g/10min 22b 12b 12b Mold shrinkage Mold 2mm thickness % 0.8 1.3 1.3 * Melt flow index a:190 b:230The data the description is the popular value, not the guaranteed value.The data the description is the popular value, not the guaranteed value.