弯头保温材料外弧段的纵向连接.docVIP

弯头保温材料外弧段的纵向连接复合硅酸盐纤维板和复合硅酸盐膏保温材料在相同工艺条件下，其使用厚度为硬质成型微孔硅酸钙保温材料的五分之三，在主蒸汽管道主保温层上，用细铁丝捆扎一层复合硅酸盐纤维板，厚度为25mm，将它错缝粘贴，并用复合硅酸盐膏保温材料涂抹保温层的缝隙，保证其保温的密封性能。在第4 层复合硅酸盐纤维板外用细铁丝网整体捆扎、勒紧，防止保温层滑动、错位。外使用复合硅酸盐膏保温材料进行厚度为10mm 的密封涂抹，形成厚度为35mm 的加强保温层。Composite silicate fiberboard and composite silicate compound heat preservation material in the same process conditions, the thickness of its use for hard three 5 of forming microporous calcium silicate insulation material, on the main steam pipe main insulation layer, with fine wire banding layer compound silicate fiberboard, thickness is 25 mm, will it be done paste, and composite silicate paste insulation materials insulation daub of aperture, assure its insulation sealing performance. In the fourth layer composite silicate fiberboard topical fine wire overall strapping, tighten, prevent the thermal insulation layer sliding and dislocation. Outside using composite silicate compound heat preservation material thickness is 10 mm sealing daub, formation thickness for the strengthening of 35 mm. 在设备或管道外表面采取保温措施后，其保温层外表面温度必须小于50℃的规定，外表面温度已经超标。保温材料性能对比成型微孔硅酸钙产品具有质地较硬、抗热震性、可塑性差，容易碎裂粉化、容重较高、材料规格种类多、材料管理工作量大等缺点。复合硅酸盐纤维板和复合硅酸盐膏产品具有质地柔软、密度低、导热系数小、优良的热稳定性及抗热震性、优良的抗拉强度、无腐蚀无污染、施工简便可塑性强、使用寿命长，受热膨胀小，外包铁皮不会有拉裂、凹凸等优点，其保温效果特别好。After the equipment or pipe outer surface heat preservation measures, the insulation must be smaller than the outer surface temperature of 50 ℃, outside surface temperature has been overweight. Heat preservation material performance comparison forming microporous calcium silicate products with a hard, poor thermal shock resistance and plasticity, shatter easily pulverization, high bulk density, material specifications, variety, materials management workload big shortcoming. Composite silicate fiberboard and composite silicate paste products with a soft, low density, low coefficient of thermal conductivity, excellent thermal stability and thermal shock resistance, good tensile strength, no corrosion, no pollution, easy construction of pl