常州大学本科生毕业计(论文)编排格式(理、工、经、管、文、法类通用).docVIP

学号： （宋体 五号 粗体） 常 州 大 学 毕业设计（论文） （2014）二○摘 要：制备了具有荷叶表面的DLC薄膜 关键词：；； Preparation and properties of mul-tiscale Bionic diamond-like carbon films (plants) Abstract：Inspired by plants in nature that show obvious superhydrophobic performance with high or low adhesion, developing artificial ways to mimic these surfaces is meaningful. In this paper, the initial sample film with lotus leaf and rice leaf texture was prepared by the replica method based on PDMS. Then, By combining electrochemical and deposition , DLC films with “lotus leaf”-like and “rice leaf”-like textures were successfully fabricated. The film was modified with PFPE to improve friction properties and hydrophobic properties. The bio-mimetic micro/nano-binary textures of DLC films were examined by 3D non-contact optical pro-filometry. The hydro-phobicity of DLC film was texted by contact angle, and friction performance was analyzed with UMT. The results show that the modified film has a high toughness and a low coefficient of friction, coefficient of friction is maintained between 0.15 to 0.2, he best can reach 0.12. Also has good super-hydrophobic (contact angle up to 155 degrees). Superhydrophobic DLC film can be used as a lubricating layer of material, but also has a low friction will be widely used in practical engineering applications. Key words：super-hydrophobic ; micro/nano-binary; coefficient of friction 目 录 摘要·········································································································································Ⅰ 目·········································································································································Ⅲ 术语表（如有）·····················································································································Ⅳ 一、引言（或绪论）·············································································································1 （一）题名··········