杨永源-光固化油墨ppt.ppt

光固化油墨 氧的阻聚 齐聚体 50-80% 颜料 4% 单体 10-30% 活性胺 3% ITX 0.5% Irg907 4.5% Total 100% 不同浓度的颜料在CN2001中分布的屈服应力 含25%颜料的环氧丙烯酸酯的粘度 不同颜料在环氧丙烯酸酯中分布的屈服应力 不同颜料在环氧中中分布的触变性 含25%颜料的聚酯丙烯酸酯的粘度 含25%颜料的聚酯丙烯酸酯的屈服应力 含25%颜料的聚酯丙烯酸酯的触变性 Color strength of yellow ink dispersions Color strength of blue inks with various acrylate monomers Color strength of red inks with various acrylate monomers Color strength of black inks with various acrylate monomers Viscosity of yellow inks with various acrylate monomers Yield value of yellow inks with various acrylate monomers Viscosity of blue inks with various acrylate monomers Yield value of blue inks with various acrylate monomers Viscosity of black inks with various acrylate monomers Yield value of black inks with various acrylate monomers Viscosity of red inks with various acrylate monomers Yield value of red inks with various acrylate monomers 结 论 对四种多醇和两种烷氧化类型的十六种丙烯酸酯单体进行彩色强度和流变性的研究, 没有得出化学结构与性能的关系, 但得到色强度, 粘度和屈服值有价值的结果。 色强度, 低粘度, 低屈服值最佳组合: 黄油墨, 黑油墨: 2PO NPGDA, 二丙氧基化新戊二醇双丙烯酸酯 蓝油墨, TPGDA 二缩三丙二醇双丙烯酸酯 MM 3EO TMPDA 三乙氧基化三羟甲基丙烷二丙烯酸酯单甲醚 红油墨 MM 3EO TMPDA 没有一个特殊的单体对四种彩色油墨都能得到最佳的性能 光固油墨助剂 泡控制助剂 改善表观 防止针孔 防止桔子皮 改善研磨, 分散过程中颜料湿润 表面控制助剂 湿润剂: 提高对基材的粘附 提高层间粘附 颜料漂浮和与树脂润湿 流平剂: 改善层间拈附 改善表观 提高光泽 助剂对固化油墨的微观结构的影响 流平剂对油墨表观性能的影响 表面活性剂对油墨性能的影响 用于研究的油墨配方： BERCRYL 3415 78.5 BERCRYL 110 11.5 ViaCure DX 5.0 Pigment Irgalite Rubine L4BD 5.0 Viscosity of the final ink: 6700 cP at 25?C 选择这个配方的主要原因是BERCRYL 3415 对各种基材（PC, PS, PVC 显示出良好的粘接性 能量转移机理 电子转移机理 部分光引发剂的结构图 新型双官能团引发剂 LFC 100 油墨的主要组成成分, “是油墨的心脏” 活性连接体: 颜料的连接料, 可光聚合成网状大分子 给油墨以理想的机械物理性能 包括: 强度, 硬度, 柔韧性, 光泽度, 耐溶剂, 耐老化, 耐磨 调节活性官能团, 提高光固化速度 给颜料以湿润, 分散和稳定作用 给油墨印刷适性:粘度, 粘性, 屈服值, 流变性, 油墨转移性能 预聚体和活性稀释单体的作用 预 聚 体 单体 预聚体官能团数对固化性能的影响 固化性能 单 双 三 四 五 六 固化速度 慢 …… …… …… …… 快 柔韧性 柔韧 …… …… …… …… 脆 硬度 软 …… …… …… …… 硬 抗溶剂性 差 …… …… …… …… 优 收缩 低 …… …… …… …… 高 Sartomer 公司用于UV胶印油墨的齐聚体产品 产品 产品级别 推荐应用 特征及功能 CN293 聚酯丙烯酸酯 柔版油墨, 胶印墨 耐磨涂料 Excellent flow characteristics and pigment wetting. Provides low