刨切微薄竹生产工艺研究.docVIP

刨切薄竹生产工艺研究 刘志坤1 李延军1 杜春贵1 文桂峰1 林勇2 （1.浙江林学院工程学院，浙江临安，311300 ; 2.杭州木材厂.浙江杭州.310009;） 摘要：为提高竹材产品的科技含量和附加值，提高资源的利用效率，将毛竹横截、纵锯、粗刨、蒸煮、干燥等工序加工成矩形断面的竹条；再经精刨、砂光、涂胶、侧拼制成侧拼单层竹片胶合板块；之后注入软化剂、竹块叠层湿胶合制得竹方；将竹方升温软化处理，在刨切机上刨切获得0.20～1.50mm，柔韧性良好，厚度均匀的刨切薄竹片，为竹材精、深加工和高效利用开辟了工业化利用新途径。刨切薄竹片可代替广泛使用的珍贵薄木用于装饰材料的贴面和家具表面装饰。 关键词：竹材加工、刨切、薄竹片、软化、竹方、胶粘剂 中图分类号： A Study on Production Technology of Sliced Bamboo Veneer Liu Zhi-kun1 Li Yan-jun 1 Du Chun-gui1 Wen Gui-feng1 Lin Yong2 (1. Zhejiang Forestry College, Lian Zhenjiang 311300；2 Hangzhou Wood factory . Hangzhou Zhenjiang. 310009) Abstract: A technology of sliced bamboo veneer is introduced. Bamboo is processed via cross cutting, rip saw, primary slicing, steaming, drying and so on planning into rectangle side bamboo strips, The strips are turned to bamboo plate plywood via smoothing slice ,sanding, glue application, increase the bamboo block’s temperature to intenerate it. After the block is processed to the even-thickness(about 0.20~1.50mm)sliced bamboo veneer with high tenacity which may be used as the finely veneer for overlaying. This technology breaks a new path for the advanced industrialized process and usage of bamboo. Key Word: Bamboo Process ,Slice, Bamboo Veneer , Softening, Bamboo Block, Adhesive 我国是一个木材资源相对贫乏，特别是优质大径阔叶材短缺，而竹材资源较丰富的国家。较长时间以来木材资源一直存在着供需紧张的矛盾，尤其是国家实施“天然林保护工程”后，这种矛盾就变得更加突出，森林资源开发利用的重点已由天然林逐步转变为速生人工林为主，因此竹材资源的开发利用得到了迅速发展。由于竹材具有生长快、材质好、色泽淡黄、高雅的特点，完全可以代替珍贵木材，因而其加工利用越来越受到人们的重视，对竹材深加工工艺的研究也更为深入[1～4]。 本研究通过实验室小试，生产厂家中试及较大规模生产试验三个阶段，分析了利用组合竹方刨切薄竹、特别是微薄竹生产工艺的可行性，确定了规模生产中竹方制备工艺及刨切技术参数。刨切微薄竹产品可代替山毛榉、樱桃木、胡桃木等珍贵木材，广泛用作装饰材料及家具、人造板等的贴面材料，为竹材的精、深加工和高效利用开辟了工业化利用新途径，为提高竹质产品的科技含量和附加值提供了强有力的技术支撑。还将为竹木复合材料开辟了广阔的发展前景。该项技术已于2002年9月、11月先后申请实用新型（申请号0）和发明专利（申请号为8）。 1 径向集成竹块制备工艺(The preparation technology of radial laminated bamboo lump) 1．1 竹条制备(Preparation of bamboo strips) 选竹龄5年生以上，直径8cm以上的新鲜、无腐朽虫柱的毛竹（也可用其它竹种）经横截、纵锯、粗刨、蒸煮、干燥（或炭化）制成矩形断面的竹坯条，竹坯条厚度4～8mm，宽度一般为18mm左右，长度根据刨切需要确定，一般为1000～