浅析水泥基珍珠吸声板开裂原因及防治措施.docVIP

浅析水泥基珍珠岩吸声板开裂原因及防治措施 孔飞1、潘钢华2、郭雷3 (1从事吸声材料制作的工程师；2东南大学材料科学与工程学院 教授 副院长；3安徽建筑工业学院材化学院 在读硕士研究生) 摘要：通过正交试验分析了骨料种类、乳液和纤维掺量对水泥基珍珠岩吸声材料的容重、抗压、抗折强度、线性收缩率的影响，其中骨料性能是影响水泥基珍珠岩吸声材料性能的主要因素，选择吸水率低、筒压强度高的轻骨料，是提高产品内聚力、降低产品收缩值，防止产品开裂的最佳方式。在骨料材质一定的前提下，可以通过调试配方，如在配方中增加纤维、乳液等增加产品内聚力，同时选择适当的产品尺寸和固定方式，也可以有效防治产品开裂。 关键词：骨料种类、产品宏观尺寸、固定方式、裂纹 Abstract: The effects of aggregate types、latex and fiber concentration on cracks of pearlite pore concrete were investigated with orthogonal experiment method, the results show that aggregate types is the more important causes on the crack, as the more press-tube strength and the less water absorption of light aggregate, the better adhesive strength of material. The influence of plate size and fixed method on crack have analyzed with?single?factor?method on condition of the same aggregate type. It concluded that the crack can be avoided no only by added latex and fiber, but by optimize proper produce size and fixed methods. Keywords: aggregate type、size、fixed9，共9组试验结果，具体见下表2、表3； 表1 骨料性能参数 材料种类 开口膨胀珍珠岩[1] 闭孔膨胀珍珠岩[1] 玻璃微珠 颗粒粒径（mm） 0.3-1.2 0.3-1.2 0.8-1.2 体积密度（kg/m3） 70 250 2600 筒压强度 76%-83% （1Mpa压力的体积损失率%）38%-46% （1Mpa压力的体积损失率%）Sika latex(L)(kg/m3) 0 15 30 纤维掺量 (F)(kg/m3) 0.3 0.6 0.9 备注：Sika latex 为SIKA胶皇；纤维长度为10mm，当量直径为30μm的束状单丝 五点法固定 三点法固定 平行线法固定 图1 粘贴固定方式 （单个粘贴面直径为100mm，平行线线粗为100mm，粘贴胶厚度为20mm） 3、试验结果及分析 3.1试验结果 3.1.1正交试验结果 标准条件20℃、相对湿度65％情况下测得28天线性收缩值（按照砂浆收缩标准试验方法测试）； 表4 正交试验结果 性 能 组 别 表干容重 （kg/m3） 抗压强度 (MPa) 抗折强度 (MPa) 线性收缩率 (mm/m) A-1 693.4 4.3 0.3 4.2 A-2 706.4 5.7 0.5 3.5 A-3 731.9 6.0 0.6 2.9 A-4 735.0 7.4 0.9 2.8 A-5 740.8 8.1 1.2 2.5 A-6 745.5 9.2 0.8 2.1 A-7 2980.8 17.3 2.1 1.0 A-8 2985.2 18.2 1.8 0.6 A-9 3000.3 19.6 2.4 0.3 表5 正交试验计算表 表干容重(kg/m3) 抗压强度(MPa) 抗折强度(MPa) 线性收缩率(mm/m) G L F G L F G L PPF G L F K1 2132 4409 4839 16 29.0 29.0 1.4 3.3 2.9 10.6 8.0 6.9 K2 2221 4432 4935 24.7 32.1 32.7 2.9 3.5 3.8 7.4 6.6 6.6 K3 8966 4477 4948 55.1 33.7 31.4 6.3