大摻量矿物掺合料在大体积基础底板中的应用.docVIP

大掺量矿物掺合料混凝土技术在北京财富中心 二期工程中的应用 刘明均 吴珍 北京双良混凝土搅拌站 【摘要】：本文介绍了矿物掺合料超过胶凝材料50%的混凝土技术在北京财富中心二期底板大体积混凝土工程中的应用情况。就原材料、配合比试验、施工配套技术、28天、60天、90天强度做了详细说明。通过研究、应用与分析，总结了近年来在大体积工程中逐渐被工程界接受的大掺量矿物掺合料混凝土的制备技术与施工技术要点。 【关键词】大掺量 矿物掺合料 大体积混凝土 制备技术 施工技术 The Application of High Volume Mineral Admixture Concrete Technology in the Second Phase project of Beijing Wealth Centre Liu Mingjun Wu Zhen (Beijing Shuangliang Concrete Mixing Plant) [Abstract] This paper introduces the application of concrete in which mineral admixture to total binding materials ratio is more than 50% in the large volume concrete bottom board of Beijing wealth centre second phase project. Raw materials, mix test, matching technology and strength at age of 28days and 60days are described in detail. Through study, application and analysis, the preparation technology and construction technique main point of high volume mineral admixture concrete which has been accepted in large volume concrete engineering by engineering field are summed up. [Key words] High volume; mineral admixture; large volume concrete; preparation technology ;construction technique. 我国当前基础设施建设中，大型混凝土结构越来越多。混凝土由于温度应力引发开裂已成为一个重要因素。在首都近几年的重要工程建设中大掺量矿物掺合料混凝土屡次应用，效果良好。围绕大掺量矿物掺合料混凝土的成套技术正在逐渐成熟和完善，低水泥熟料混凝土技术今后的应用领域绝不仅是大体积混凝土工程。在更多的混凝土结构与混凝土制品中应用是大势所趋，这是循环经济和低碳发展模式下的必然选择。正如覃维祖教授所讲［1］：要想从整体来全面有效地解决问题，得大幅度改善混凝土结构的耐久性，使混凝土技术得到可持续发展，就需要开发与应用既能满足早期强度发展需要，又能显著降低水化温升、减小开裂风险;既能大幅度减少熟料水泥用量，又能大规模利用工业废料，既经济又环保的混凝土技术，而大量工程实践已经证明:大掺量粉煤灰混凝土正是这样的混凝土材料。通过不断总结和宣传此项技术在工程中应用情况，对于促进绿色混凝土技术的广泛应用具有积极的推动和示范作用。北京财富中心二期工程底板厚度为3500mm,局部厚度为7600mm、5000mm和1500mm，车库底板厚度为1500mm、1200mm和900mm，底板混凝土总量为16290m3,其中主楼底板混凝土浇注体积13000m3，混凝土等级C40P10。依据《混凝土强度检验评定标准》（ 1 原材料 1.1水泥 试验采用冀东水泥有限公司生产的42.5#普通硅酸盐水泥。其主要物理性能见表1。 表1 水泥的主要物理性能 标准稠度 用水量 初凝时间 终凝时间 细度(80) 安定性 (雷式法) 抗折强度(MPa) 抗压强度(MPa) 3d 28d 3d 28d 28% 163min 215min 3.6% 合格 6.3 9.2 28.8 51.4 注：水化热247kJ/kg 1.2粉煤灰 试验使用的是Ⅰ级粉煤灰，主要物理性能见表2 表2 粉煤灰主要物理性能 细度(45μm筛余量，%) 烧失量% 需水量比（%） 表观密度(g/cm3) 7.9 3.7 90 2.14 1.3矿粉 试验