* * The polymer emulsion, at 175°F, is sprayed on the road surface. Weve supplied Stylink CRS-2P for the process; anionic emulsions can also be used. The hot mix is placed immediately (within 3 seconds) after the emulsion. Laydown temp = 280-315°F. May use Stylink in HMA for extra durability on high volume highly stressed applications Paver is specific to system, but hot mix is made using conventional plant. Pavers made under license from the patent holder. Paver includes emulsion storage tank, emulsion spray bar and necessary pumps and electronics for accurate continuous application of the emulsion and HMA （6）改性沥青的生产工艺 直接混溶法：采用直接混溶法制作改性沥青，采用的共混设备有搅拌机和胶体磨两种。 母料法：余弦制作改性剂浓度较高的改性沥青母体，运输到现场后经稀释后使用，即改性沥青的母料制作法。 胶乳法：采用丁苯胶乳（浓度高的胶体乳液）直接投入沥青混合料拌合机内与矿料、沥青拌合制作改性沥青混合料。 （1）概述 定义：是粘稠沥青经热熔和机械作用以微滴状态分散于含有乳化剂-稳定剂的水中，形成水包油（O/W）型的沥青乳液。 优势：① 可冷态施工，节余能源。粘稠沥青通常要加热至160～180℃施工，而乳化沥青可以在常温下进行喷洒、贯入或拌和摊铺，现场无需加热，简化了施工程序，操作简便，节省了能源。② 可在潮湿基层上使用，能直接与湿集料拌和，粘结力不会减低。而用其它沥青施工，必须在干燥的基层或干燥的集料拌和才能保证有足够的粘结力。③ 无毒、无嗅、不燃、施工安全，保护环境，减少污染。④ 节省能源、降低成本、增加结构沥青。 （1）概述 缺点：① 稳定性差，贮存期不超过半年，贮存期过长容易引起凝聚分层，贮存温度在0℃以上。② 乳化沥青修筑路面成型期较长，最初应控制车辆行使速度。 应用：不仅可用于路面的维修与养护，并可用于铺筑表面处置、贯入式、沥青碎石、乳化沥青混凝土等各种结构形式的路面，还可用于旧沥青路面的冷再生，防尘处理。 （2）乳化沥青的组成材料 沥青 乳化剂 阴离子型乳化剂 阳离子型乳化剂 两性离子型乳化剂 非离子型乳化剂 稳定剂：为防止已经分散的沥青乳液在贮存期彼此凝聚，以及在施工喷洒或拌和的机械作用下有良好的稳定性，必要时加入适量的稳定剂。稳定剂可分为两类：有机稳定剂 、 无机稳定剂。 水：水是乳化沥青的主要组成部分。水在乳化沥青中起着润湿、溶解及化学反应的作用。所以要求乳化沥青中的水应当纯净，不含其它杂质，一般要求用每升水中氧化钙含量不得超过80mg的洁净水，否则对乳化性能将有很大的影响，并且要多消耗乳化剂。水的用量一般为30%～70% （3）乳化沥青的形成机理 乳化剂降低界面能的作用 界面膜的保护作用：具有较长烷基链的乳化剂与沥青具有较好的吸附作用，因此容易形成紧密排列，从而增强了界面膜的强度，保护沥青微粒不致由于碰撞而聚集。界面膜强度和紧密程度：取决于乳化剂分子结构和浓度。 界面电荷的稳定作用：由于乳化剂的作用，在沥青与水界面上形成双电层结构。因此在沥青液滴相互碰撞时，由于排斥作用阻止了沥青液滴的聚集，保证了沥青乳液的稳定。双电层电位差决定了扩散层的厚度，双电层厚度越大，乳液的稳定性越强。 （3）乳化沥青的破乳机理 电荷理论：阴离子乳液（沥青微滴带负电荷）与带正电荷碱性集料（石灰石、玄武石等）具有较好的粘结性；阳离子乳液（沥青微滴带正电荷）与带负电荷的酸性集料（花岗岩、石英石等）具有较好的粘结性。同时与碱性集料也有较好的亲和力。 水分蒸发：由于水分蒸发或被石料吸收而产生分解、破乳，多孔、干燥的集料易吸收水分，破坏乳液平衡，加速破乳。 （3）乳化沥青的破乳机理 酸碱中和（化学反应理论）：阳离子沥青乳液有一定的游离酸 ，pH较小，游离酸与碱性集料发