海藻酸钠与纳米晶纤维素共混膜制备与性能研究.docVIP

海藻酸钠与纳米晶纤维素共混膜制备与性能研究 第一作者地址：山东省青岛市市南区青岛大学 ： （1 青岛大学纺织学院，山东青岛266000 2 青岛大学纺织学院，山东青岛266000） 摘要 借助冷冻干燥技术制备了海藻酸钠与纳米晶纤维素共混膜以达到增强目的；探讨了不同含量的纳米晶纤维素与海藻酸钠共混膜的微观形貌、力学性能、吸水性能及孔隙率的变化；综合评价确定最佳的纳米晶纤维素含量在0.75%至1.00%之间。 关键词 海藻酸钠 纳米晶纤维素 共混膜 增强 中图分类号：TS201.2 文献标识码：A Research on the Preparation and Property of Sodium Alginate Membranes with Nanocrystalline Cellulose SUN Tingting1，ZHOU Rong2，ZHANG Yuanming2 （1、QingDao University College of Textiles，Qingdao 266000 2、QingDao University College of Textiles，Qingdao 266000） Abstract Blend the oxide of the sodium alginate after freeze drying with different quality of Nanocrystalline Cellulose ,make those into membranes by freeze drying technology ,the membranes must be dipped into calcium chloride called crosslinking process.The membranes were prepared by different content.Finally test basic properties of different membranes, and compare with alginate membranes.The main goal is enhancing, controlling the content of Nanocrystalline Cellulose and strength,,elongation at break and water-absorption rate ,achieve the optimum content of Nanocrystalline Cellulose .Experimental results show that with the increasing content of nanocrystalline cellulose , the micro structure changes, tensile strength and elongation at break increases first then decreases, water-absorption rate, porosity ratio decreases first and then increases,the critical point is 1%, comprehensive consideration, the best content is between 0.75% to 1%. Key words sodium alginate sanocrystalline cellulose membranes enhancing 0 引言 人类步入21世纪后，火灾，意外伤害等带来的皮肤问题越来越多，各种有关皮肤创伤的问题逐渐引起了人们对皮肤组织工程[1]的兴趣和需求。 皮肤组织工程支架是皮肤组织工程的极为重要组成部分，目前工程支架有胶原类，壳聚糖类，透明质酸类，海藻酸盐类[2]，它们都具有生物相容性。其中海藻酸盐类具有很好的免疫原性，安全无毒，被广泛使用。其一般利用水为介质，通过冷冻干燥法形成多孔三维结构。然而此种方法制得的材料强度较低，因此通常采用添加纤维素，壳聚糖，聚乙烯醇等作为增强体[3]的方法改性。纤维素由于来源广被广泛应用，本研究将纤维素控制在纳米尺寸制得纳米晶纤维素，从而使其具有小尺寸效应等优势。纳米晶纤维素与海藻酸钠共混膜具有很好的研究价值。 本研究主要目的是通过添加纳米晶纤维素以实现增强处理，同时增加膜的不溶性。结合其