examintion.docVIP

List the chemical composition requirement for the grades of the order, And the chemical composition difference between 304, 304L, 316, 316L, 304/L and 316/L. Answer the question: The chemical composition requirement for the grades of the order are listed in the below table 1 and grades 304,304L,316,316Lof the chemical composition are listed in the below table 2 and their different of chemical composition will be see from in the table 2. STABLE 1 Standard Element name Grade 304 316 304/L 316/L 310S ASTM A269/213 Carbon ≤0.08 ≤0.08 ≤0.035 ≤0.035 ≤0.08 Composition,% Manganese ≤2.00 ≤2.00 ≤2.00 ≤2.00 ≤2.00 Phosphorus ≤0.045 ≤0.045 ≤0.045 ≤0.045 ≤0.045 Sulfur ≤0.03 ≤0.03 ≤0.03 ≤0.03 ≤0.03 Nickel 8.0-11.0 10.0-14.0 8.0-11 10.0-14.0 19.0-22.0 Chromium 18.0-20.0 16.0-18.0 18.0-20.0 16.0-18.0 24.0-26.0 Molybdenum - 2.0-3.0 - 2.0-3.0 - Silicon ≤1 ≤1 ≤1 ≤1 ≤1.00 STABLE 2 Standard element names 304 304L 316 316L 304/L 316/L composition,% ASTM A269/213 Carbon ≤0.08 ≤0.035 ≤0.08 ≤0.035 ≤0.08 ≤0.08 Manganese ≤2 ≤2 ≤2 ≤2 ≤2 ≤2 Phosphorus ≤0.045 ≤0.045 ≤0.045 ≤0.045 ≤0.045 ≤0.045 Sulfur ≤0.03 ≤0.03 ≤0.03 ≤0.03 ≤0.03 ≤0.03 Nickel 8.0-11 8.0-12 10.0-14.0 10.0-14.0 8.0-11 10.0-14.0 Chromium 18.0-20.0 18.0-20.0 16.0-18.0 16.0-18.0 18.0-20.0 16.0-18.0 Molybdenum 2.0-3.0 2.0-3.0 2.0-3.0 Silicon ≤1 ≤1 ≤1 ≤1 ≤1 ≤1 2. List the heat treatment requirement for different grades under the Order. Answer the question: All austenitic tubes shall be furnished in the heat-treated condition and shall be heat treated in accordance with the requirements of the below table 3. Alternatively ,immediately after hot forming ,while the temperature of the tubes is not less than the minimum solution treatment temperature specified in the blow table3,tubes may be individually quenched in water or rapidly cooled by other means. Table 3 Grade Heat Treat Type Solutioning Temperature min or range 。F（℃） Cooling Media 304 Solution Treatment 190