底吹炉处理锌浸出渣工艺设想 河南豫光金铅股份有限公司 河南济源 454650 ［摘要］目前主流的湿法炼锌工艺对产出的浸出渣采用回转窑挥发法处理存在成本高、焦耗大、有价金属回收率低等诸多缺点，有待开发新的工艺装备及工艺进行更新换代。本文论述采用底吹熔池熔炼工艺处理湿法炼锌浸出渣工艺过程及其原理，并对关键工艺要点展开讨论，并与常规回转窑挥发法处理工艺进行比较，确定了采用底吹熔池熔炼工艺处理浸出渣的可行性。 ［关键词］湿法炼锌；浸出渣；回转窑；底吹炉；熔池熔炼；工艺设想 Technology idea on treatment of leaching residue of zinc hydrometallurgy by bottom-blown furnace abstract:Current mainstream hydrometallurgy of zinc leaching residue by rotary kiln volatilization method has many disadvantages such as high treatment cost, high coke consumption and low metal recovery, pending the development of new technology and equipment for the replacement. This article discusses the idea of treatment processes and principles by using a bottom blowing bath smelting process to treat the hydrometallurgical zinc leaching residue, and discuss the key process elements, and compared with conventional treatment by rotary kiln volatilization process, identified the use of bottom blowing feasibility of bath smelting process for leaching residue treatment. Keywords: hydrometallurgy of zinc; leaching residue; rotary kiln; bottom-blown furnace; bath smelting; process idea 0、前言 锌冶炼的方法有火法炼锌和湿法炼锌两种，其中湿法炼锌在世界范围内已占锌冶炼总量的80%以上。近年来我国新增锌冶炼产能也是以湿法炼锌为主。湿法炼锌已成为世界锌冶炼生产的发展方向。而湿法炼锌生产中所得到的大量浸出渣中含有较多的锌及其它有价金属。为了充分利用资源，提高金属回收率和其它有价金属的综合回收利用，必须对浸出渣进行处理。浸出渣处理的方法很多，目前采用最为广泛的是回转窑挥发法，该法处理存在成本高、焦耗大、有价金属回收率低等诸多缺点，有待开发新的工艺装备及工艺进行更新换代。 1、锌浸出渣来源及成份 1.1锌浸出渣来源 某电锌生产厂设计产能20万t/a，采用典型的“焙烧—浸出—电积—铸型”湿法炼锌工艺生产。在这种常规湿法炼锌流程中，焙砂中几乎全部的铅、金、银、铟、锗、镓，60%的铜、30%的镉、15%的锌都进入浸出渣中。锌精矿的锌品位处于47.5%~49%之间，按每生产1t电锌可以产出1.0~1.05t浸出渣，电锌产能20万t/a规模，则每年产出浸出渣约为20~21万t。 1.2浸出渣的成份及属性 锌浸出渣的化学组成和锌物相组成分别见表1和表2。从分析结果可知，锌浸出渣中锌的含量较高，并含有Pb、Cu、Fe、Au、Ag等有价金属与贵金属。 表1 锌浸出渣的化学成份 Tab.1 Chemical composition of leaching residue of zinc 成份 Zn Pb Cu S Fe SiO2 CaO Au（g/t） Ag（g/t） 水份 含量% 20~22 2~4 0.8~1.2 5~6 21~23 8~12 3~5 0.1~0.8 100~300 16~18 表2 锌浸出渣中的锌物相组成 Tab. 2 The thing is composed of Zn each other in leaching residue of zinc 成份 ZnO·Fe2O3 ZnS ZnSO4 ZnO ZnO·SiO2 含量（%） 42.40