搅拌摩擦焊技术 鲍雷 （黄山学院机电学院，安徽，黄山，245000） 摘要：搅拌摩擦焊（Friction Stir Welding,简称FSW）是英国焊接研究所（The Welding Institute）于1991年发明的专利焊接技术。搅拌摩擦焊除了具有普通摩擦技术的优点外，还可以进行多种接头形式和不同焊接位置的连接。本文论述了搅拌摩擦焊的基本原理、特点和发展现状。 关键词：搅拌摩擦焊；基本原理；特点；发展现状 Friction Stir Welding BaoLei (School of mechanical engineering of Huangshan University，Anhui，Huangshan 245000,China) Abstract:Friction Stir Welding (Friction Stir Welding, referred to as FSW) is the Welding Research Institute of England (The Welding Institute) in 1991 invention patent welding technology. Friction stir welding besides the advantages of conventional friction technology, can also be used for a variety of different position of welding joints and connections. This paper discusses the basic principle, characteristics and development status of friction stir welding. Key words:Friction Stir Welding;fundamental;characteristic;development situation 摩擦焊是利用工件端面相互运动、相互摩擦所产生的热，使端部达到热塑性状态，然后迅速顶锻，完成焊接的一种方法。摩擦焊可以方便地连接同种或异种材料，包括金属、部分金属基复合材料、陶瓷及塑料。摩擦焊方法在制造业中已应用40多年了，由于其生产率高、质量好获得了广泛的工程应用，但焊接的对象主要是回转形零件，虽然也有其它形式的摩擦焊技术出现，以克服被焊工件几何形状的限制或提高生产率，如相位摩擦焊、径向摩擦焊、线性摩擦焊等，但实际应用很少。最近还出现了摩擦堆焊，在工件上形成特殊性能的表面层。 焊接过程中不需要其它焊接消耗材料，如焊条、焊丝、焊剂及保护气体等。唯一消耗的是焊接搅拌头。　　　　 [3]汪建华,姚舜,魏良武,戚新海.搅拌摩擦焊接的传热和力学计算模型[J].焊接学报， 2000,21（4）：61-64. [4] Thomas W M,Nicholas E D,Needham J C,et al.Improvements relating to friction welding(TWI)[C].European Patent Specification 0 615 480 B1. [5]Midling O T,Morley E J,Sandvik A.Friction stir welding(Norsk Hydro,rights transferred to TWI)[C].European Patent Application 959 078 88.2. [6]章霞译.搅拌摩擦焊VS.熔焊[J].现代焊接,2006,41(5):20-21.