连续太阳辐射影响下混凝土温度仿真计算 　　摘要：高温季节浇筑混凝土时，气温和太阳辐射对混凝土浇筑后温度影响大。模拟了某工程非溢流坝段碾压混凝土的浇筑过程，就有无考虑连续太阳辐射影响下、不同持续太阳辐射时间下混凝土表面点与内部点温度过程进行了仿真计算。结果表明：连续太阳辐射对混凝土的影响深度是有限的；由太阳辐射引起混凝土表面最高温度升高值前期增长幅度大后期增长小。 　　Abstract: high temperature season during the pouring of concrete, temperature and solar radiation effect on the temperature of concrete. Simulation of the construction process of an engineering non-overflow dam section of roller compacted concrete, there is no consider the influence of continuous sun radiation, solar radiation under different time points on the surface of concrete and internal temperature process simulation calculation. The results show that: the influence of solar radiation on concrete depth is limited by the maximum temperature; concrete surface increased value in early growth greatly small late growth by solar radiation. 　　 　　关键词：太阳辐射混凝土 影响深度 　　中图分类号：[TQ178]文献标识码：A 文章编码 　　夏季混凝土施工的仓面很大, 混凝土暴露时间长, 受太阳辐射的影响严重。太阳辐射可使碾压混凝土层面气温平均每小时上升5℃[1]；浇筑季节的不同，太阳辐射对混凝土的影响差别较大；浇筑层层间歇时间，是太阳辐射对混凝土影响的直接因素；入仓温度的高低，只影响混凝土的最高温度，不影响有无太阳辐射下混凝土的最高温度的差值[2]。在我国西北部分地区夏季高温不低，太阳辐射强。本文结合具体工程实例计算了不同持续时间下太阳辐射影响表面和内部混凝土的温度变化，对实际施工具有参考意义。 　　1.工程概况 　　党恩水电站位于巴楚河上游，坝址海拔在2700m～4090m之间，其地理位置介于东经99°03′~99°43′、北纬29°48′~30°37′之间。因太阳辐射严重，夏季最高温度不低。 　　1.1气温资料 　　根据提供的气温资料，为了便于计算，拟合出气温公式如下，拟合效果图见图1： 　　 　　其中――气温（℃）； 　　――时间，单位（天）。 　　 　　图 1实测月平均气温及拟合效果 　　 　　1.2太阳辐射日际变化 　　党恩电站位于纬度在29°~31°之间，太阳辐射热月平均值6月份最高，12月份最低，但气温在7月份最高，为研究在高温情形下太阳辐射热对混凝土的影响，故选取7月份的太阳辐射做典型分析，假定太阳辐射热在1d内的是按余弦分布的[1],见下式。 　　(1) 　　其中 　　式中：0.65为混凝土表面的吸收系数[3]；为一天之内日照延续时间，7月份取14h,为晴天太阳辐射热，这里取1311.2为系数，这里取0.68；为云量，取0.2；表面放热系数取62.5。 　　2.计算模型和浇筑计划 　　2.1计算模型 　　坝体混凝土浇筑块，选取立方体块，每3m高一仓分10个浇筑胚层。坝体单元类型为六面体8节点等参单元。为了充分考虑夏季气温日际变化对浇筑块温度场的影响，将计算步长定为1/8d (3h)。在ANSYS中建立的计算网格如图2所示。 　　 　　图2 计算模型 　　2.2材料参数 　　根据所给资料，计算模型混凝土的基本参数见表1 　　表 1材料的基本参数 　　 　　 　　碾压混凝土C25绝热温升公式如下： 　　（2） 　　混凝土弹模公式如下： 　　 （3） 　　基岩弹模取42.5GPa. 　　2.3计算工况 　　为了研究不同持续时间太阳辐射影响下对混凝土温度的影响，采用以下4种方案进行仿真计算。工况1-4均是自然浇筑，工况1不考虑太阳辐射；工况2、3、4分别从2012-7-12开始考虑连续2、4、6天太阳辐射热的影响，见表2。 　　表