混凝土早期收縮性能研究.docVIP

混凝土早期收缩性能研究 作者：杨伟东 陈岩 （单位）哈尔滨鸿成商品混凝土有限公司 哈尔滨鸿成商品混凝土有限公司 摘要：本文依据国家标准GB/T50082-2009研究强度等级及大掺量混合材对混凝土早期收缩性能的影响。结果表明混凝土早期总收缩随强度等级的提高而增加；和基准混凝土相比，混凝土中掺加30%矿粉和20%粉煤灰后早期总收缩值有所增加，但均不大。混凝土早期总收缩主要发生在24h内， 24h内混凝土收缩显著。强度等级高的混凝土早期失水情况较为严重，掺加大掺量粉煤灰和矿粉后，早期水分流失进一步增加。 关键词：混凝土；早期收缩；粉煤灰；磨细矿渣 Research on early shrinkage of concrete Abstract: Effect of high volume admixture and strength grade on early shrinkage of concrete was researched according to GB/T50082-2009 lock in this paper.The results showed that early total shrinkage of concrete was increased with increase of strength. The shrinkage was increased a little after mixed with 30% slag and 20% fly ash compared to the control concrete.The total shrinkage of concrete mainly occurs within 24h and shrinkage was significant. Water loss of high-strength grade concrete was more serious. The early loss of water further increased after the fly ash and slag was mixed into concrete. Keyword: Concrete, Early shrinkage, Fly ash, Slag 1.前言 混凝土早期收缩和开裂越来越引起人们重视，早期收缩产生的主要原因为混凝土的水灰比较小、单位体积内水泥用量较大、水泥细度不断提高、减水剂、早强剂的使用。这些都提高了混凝土的早期强度及其发展速度，提高了混凝土的早期水化热，导致了混凝土早期收缩。混凝土早期收缩的发生过程为：水泥的水化、混凝土水分的迁移、局部水分缺乏、混凝土内毛细孔表面张力的增大、混凝土发生早期收缩。在整个收缩发生过程中，控制其中任何一个环节都能够改善混凝土早期收缩的发生。目前，活性混合材已广泛应用于混凝土中[1-3]，但一般掺量较少，尤其在水利工程中。由于工业废渣如粉煤灰、磨细矿渣等混合材颗粒较细， 具有火山灰活性，在混凝土中能够起到微集料效应。并且能与水泥水化过程中析出的氢氧化钙进行“二次反应”，水化产物能够填充水泥石的毛细孔，形成紧密的混凝土微观结构，提高混凝土的密实度。本文研究混凝土强度等级和混合材对混凝土早期收缩的影响，为工程施工提供必要的建议和指导。 2试验方案 2.1原材料 所用水泥为P·O 42.5型普通硅酸盐水泥；粉煤灰为Ⅰ级灰； 选用富布斯建材有限公司生产的S95级高炉矿渣；超塑化剂选用NAFR型高效减水剂，推荐掺量为胶凝材料总重量的0.8~1.5%。粗骨料为碎石，连续级配，表观密度为2660kg/m3；细骨料为江砂，细度模数2.8。混凝土搅拌用水为哈尔滨饮用自来水。 2.2试验方法及过程 将原材料按表1所示配合比均匀搅拌后分别成型抗压强度、收缩及表面蒸发量试验的混凝土试件。抗压强度采用100mm的立方体试件，分别测量3d、7d、28d、56d龄期的抗压强度。混凝土的早期收缩依据国家标准GB/T50082-2009《普通混凝土长期性能和耐久性能试验方法标准》进行。收缩试验采用100mm×100mm×400mm试模，每组3个试件，测量仪器为千分表，混凝土浇筑6h后开始测量早期收缩，每隔1h测量1次。混凝土早期表面水分蒸发量试验采用面积为100cm2的容器，在容器中浇筑混凝土，插捣后表面抹平，置于与收缩试件同一环境中，每个配合比成型3个试件。成型后称量试件的质量，6h后每隔1小时称1次重量。混凝土表面水分蒸发量为单位面积混凝土的水分蒸发质量，Kg/m2。 2.3配合比 根据试验要求，设计混凝土配合比如表1所示： 表1 混凝土配合比 编号