【2017年整理】杜邦耐盐水腐蚀性测试.docVIP

DUPONT TEFLON. FINISHES GLOBAL COOKWARE TEST METHOD PROTOCOL TITLE: SALT CORROSION TEST PROTOCOL耐盐水腐蚀性测试 GCTMP NUMBER : 02 REVISION NUMBER : 2 DATE OF REVISION : February 8, 2002 DATE OF EXPIRING: February 8, 2005 FILE: GCTMP02-SALT CORROSION ¨C REV2.DOC WRITTEN BY : GLOBAL TEST TEAM MODIFIED BY : QPT TEAM APPROVED BY: SEGMENT PRODUCT LEADER: Martina M. Welcher REFERENCE: BRITISH STANDARD BS 7069 Appendix C. Corrosion- Modified (1) PURPOSE 目的 To provide a method for testing the corrosion resistance of non-stick coating systems. 用来测试不粘涂料的耐盐水腐蚀性。 (2) PRINCIPLE 原理 Exposure of coating systems to a boiling 10% NaCL (salt) solution for a total of 24 hours. 喷涂一指定涂料体系的锅子中，盛放10%的氯化钠（盐水）溶液，煮沸24 hrs。 (3) APPARATUS 仪器 3.1 Heat source 热源 3.2 10% NaCL solution 10 %的氯化钠溶液 3.3. De-ionized Water 去离子水 (4) PREPARATION 准备 4.1 Prepare test specimens in accordance to the procedure outlined on the product fact sheet for proper application, drying and baking of the specified Teflon. system. 按照产品技术说明书的程序要求正确准备测试样品，干燥并烘烤指定的特富龙涂料体系。 4.2 Prepare 10% by weight, salt solution by combining 8 tablespoons (106 gr) Table Salt and 4 cups (960 gr) de-ionized water. 将8汤匙（106 gr）食盐溶解于4杯去离子水中以得到重量百分比10%的食盐溶液。 4.3 Prepare a mild dish detergent solution with tap water. 用去离子水配备适度浓度的洗涤剂溶液。 (5) PROCEDURE 程序 5.1. Wash the test specimens in dish detergent solution. 用洗涤剂清洗测试样品。 Rinse in cold water. 冷水淋洗测试样品。 Dry thoroughly. 完全干燥。 Visually inspect coating surface for surface defects.用肉眼检查涂料表面缺陷。 Draw a diagram of the test specimen surface. 用圆规画出测试面积表面草图。 Record all surface imperfections on the reference diagram. 在草图上标出所有的表面缺陷。 5.2 Pour the 10% salt solution into the clean test specimen to a level past the midway point of the side wall of the vessel. 倒入10%的食盐水溶液于测试样品中，至少要达到其内壁一半的高度 Mark the water level on the side wall of the test specimen. 在测试样品内壁标注水面高度 Cover the test specimen with a lid. 盖上盖子。 5.3. Place the test specimen on the heat source. Boil the solution for 24 hours. 将测试样品放在热源上，加热溶液24hrs。 Boil