新型永磁干式强磁选机在长石除铁中的试验研究彭会清，胡淼，刘艳杰.doc

新型永磁干式强磁选机在长石除铁中的试验研究 彭会清，胡淼，刘艳杰 （武汉理工大学资源与环境工程学院湖北 武汉430070） 摘 要：介绍了一种新型永磁干式强磁选机的结构和分选原理，并利用该磁选机对长石进行了除铁试验。结果表明，原矿矿样经过一粗一精除铁试验后，长石中Fe的含量从0.54%降低到018%，除铁率达到72.52%，精矿产率达到82.45%，取得了较好的分选指标。说明该磁选机除铁效果良好，设计合理。 关键词：永磁干式强磁选机；除铁；长石 TD457 文献标识码：B 文章编号：1 001—3954(2011)06—0095—04 Experimental study on iron removal from feldspar with new—type dry high-intensity permanent magnetic separator PENG Huiqing，HU Miao，LIU Yanjie School ofResourcesEnvironmental Engineering.Wuhan University ofTechnology, Wuhan 430070，Hubei，China Abstract：The structure and separation principle of a new-type dry high-intensity permanent magnetic separa- tor are introduced，and the experiment in iron removal from feldspar is carried out with the separator.After one time primary concentration and one time fine concentration，the content of Fe203 reduces from 0.54%to 0.1 8%. The good separation indexes are obtained with iron removing ratio reaching 72.52%，and the concentrate yield reaching 82.45%.The experimental results show that the separator has excellent iron removing performance and reasonable design. Keywords：dry high·intensity permanent magnetic separator；iron removal；feldspar 陶瓷的生产原料，具有较高的经济价值。而Fe203的含量多少，是评价长石矿质量优劣的Fe2030.3%[2]。根据 目前，上主要有2种磁选设备，即电磁式和2种磁选机的主要区别是，二者采用的磁 新型干式永磁强磁选机试验样机，突破了传统的2倍，保；带型可变，磁系可变，可以适应 1 新型永磁干式强磁选机 1.1结构和分选原理 1所示，包括给1.架机 2.给矿输送带轮 3.给矿输送带 4.矿粒松散弧形块 5.给矿斗 6.下磁系 7.上磁系 8.精矿输送带 9.精矿输送带轮 10.尾矿斗 11.精矿斗 图1 新型永磁干式强磁选机构 Fig1 Steucture of new-type dry high-intensity permanent magnetic separator 该磁选机采用永磁磁系，材料选用高性能钕铁硼N-S交替排N-S排列，磁极距可调；给矿物料运输 选矿时，矿粒通过松散弧形板4均匀地输送到给3上，非磁性和磁性颗粒均匀地输送到上下ll中，微 为保证良好的分选效果，该机在给矿过程中，设3，确保给矿斗5中出来的矿粒均 1.2 磁场特性 分别调节磁盘间距为10，12，15。9个点作HT201数字便携式高斯计9个点进行测量。测量结果如表所列。esults of magnetic field of separating space 1 2 3 4 5 6 7 8 9 10 1.80 1.95 1.77 1.86 2.09 1.88 1.82 1.95 1.79 12 1.69 1.87 1.70 1.80 1.89 1.83 1.75 1.83 1.59 15 1.48 1.75 1.57 1.69 1.79 1.76 1.62 1.69 1.53 由表l可知，随着磁极间距的增加，磁选空间2.09T。这是由于磁体主要集中在这一区域，因而磁