Material Sciences 材料科学, 2016, 6(6), 442-448
Published Online November 2016 in Hans. /journal/ms
/10.12677/ms.2016.66055
Research on the Sintering Process
of the Zirconia Ceramics Tape Casting
Uropatagia as the Backboard
of the Mobile Phone
Xianbo Huang, Guangyuan Xie, Peng Zhao, Li Gong, Hanyue Lin, Cong Du
Qingshan Campus, Wuhan University of Science and Technology, Wuhan Hubei
th th th
Received: Nov. 5 , 2016; accepted: Nov. 27 , 2016; published: Nov. 30 , 2016
Copyright ? 2016 by authors and Hans Publishers Inc.
This work is licensed under the Creative Commons Attribution International License (CC BY).
/licenses/by/4.0/
Open Access
Abstract
This paper compares and analyzes the relationship between the deformation of the zirconia tape
casting uropatagia used as the mobile phone backboard during the sintering process and three
placing modes including free placement, ballasting placement and placing baffle a certain height
fromuropatagia, and it also researches the smoothing process used for smooth the warping zirco-
nia backboard of the mobile phone. The result showed that ballasting placement and placing baffle
a certain height from uropatagia can be used to restrain the deformation of the zirconia tape cast-
ing uropatagia used as the mobile phone backboard during the sintering process. Among it, bal-
lasting placement was not suitable for the sintering of large-area tape casting uropatagia; and the
zirconia tape casting uropatagia sintered by means of placing baffle a certain height from uropa-
tagia could be made into relatively smooth mobile phone backboard after the smoothing process,
maintaining sintering temperature at 1400?Cfor four hours.
Keywords
您可能关注的文档
- (1-x)(K0.5Na0.5)NbO3-xBa0.985La0.01TiO3无铅陶瓷的微观结构及电性能研究.pdf
- 钙钛矿CH3NH3PbBr3电子结构和光吸收特性的第一性原理研究.pdf
- 光学增透和增反多层膜的设计与计算.pdf
- 海藻酸钠对亚甲基蓝的吸附性能研究.pdf
- 环氧改性聚氨酯树脂技术研究.pdf
- 颅骨修复钛网表面PDA_CPP涂层的制备及性能研究.pdf
- 镁基表面微弧氧化陶瓷膜的摩擦磨损特性.pdf
- 镁基类离子液体制备及物化性质的测定.pdf
- 喷雾干燥法制备LiNi0.5Co0.2Mn0.3O2正极材料及其性能研究.pdf
- 取向生长TiO2阵列薄膜的致密度和薄膜电阻调控研究.pdf
文档评论(0)