Material Sciences 材料科学, 2017, 7(1), 99-105 Published Online January 2017 in Hans. /journal/ms /10.12677/ms.2017.71013 Research for Epoxy Modified Polyurethane Resin Technology Xiaogang Zhang, Xiaoming Wang, Gui’en Zhang The 33rd Research of China Electronic Technology Group Corporation, Taiyuan Shanxi rd th th Received: Jan. 3 , 2017; accepted: Jan. 16 , 2017; published: Jan. 19 , 2017 Copyright ? 2017 by authors and Hans Publishers Inc. This work is licensed under the Creative Commons Attribution International License (CC BY). /licenses/by/4.0/ Open Access Abstract The epoxy modified polyurethane resin can be prepared under the catalyst action of isocyanate monomer and linear thermoplastic polyurethane elastomer and bisphenola epoxy resin. Through the micrograph analysis: the preparation of resin membrane surface is glossiness higher and pore less. Through the adhesion testing analysis: the adhesion of prepared resin mold on the surface of metal matrix and polymer matrix is level 0; through the calculation of collected low boiling of chromatographic analysis reaction process, the grafting rate reaches 65%. Keywords Bisphenola Epoxy Resin, Isocyanate, Grafting 环氧改性聚氨酯树脂技术研究 张小刚，王晓明，张贵恩 中国电子科技集团公司第三十三研究所，山西 太原 收稿日期：2017年1月3 日；录用日期：2017年1月16 日；发布日期：2017年1月19 日 摘 要 异氰酸酯单体、线型热塑性聚氨酯弹性体、双酚A型环氧树脂在催化剂的作用下，可制备出环氧改性聚 文章引用: 张小刚, 王晓明, 张贵恩. 环氧改性聚氨酯树脂技术研究[J]. 材料科学, 2017, 7(1): 99-105. /10.12677/ms.2017.71013 张小刚 等 氨酯树脂。通过显微照片分析：制备树脂膜表面的光泽度更高，孔隙更少。通过附着力测试分析：制备 树脂模在金属基、高分子基表面的附着力为0级；通过对色谱分析反应过程中收集到的低沸物进行计算， 环氧改性聚氨酯树脂接枝率达到65%。 关键词 双酚A环氧，异氰酸酯，接枝 1. 引言 环氧改性聚氨酯